Abstract:Nickel-based superalloys, especially single-crystal (SC) ones, have long been recognized as important materials for turbine blades used in aerospace and gas engines. Static magnetic fields are effective at controlling the material forming. The use of static magnetic fields during solidification has evolved as a sophisticated approach for efficiently controlling the microstructures and mechanical performance of metallic materials. In recent years, studies have shown that static magnetic fields have a complex effect on dendrites in SC superalloys. However, the mechanism of static magnetic fields regulating stray grains on remelted interface needs to be investigated further. This work studied the generation of stray grains near the seed remelted zone and the evolution mechanism during the directional solidification of the SC superalloy assisted by a magnetic field by tracing the solidification microstructure. The stray grains of large orientation that deviated from the <001> direction appeared on the remelted zone interface of the solidification microstructure when the magnetic field was applied, accompanied by the formation of a large-angle grain boundary (LAGB). Most of the stray grains were distributed at the sample edge. The increase in magnetic field intensity and pulling speed increased the number of stray grains and the length of the LAGB. As the solidification progressed, the large-orientation stray grains and the LAGBs were eliminated at a fast speed and evolved into small-orientation dendrites. During the following solidification, the orientation of the dendrites became even smaller and the evolution speed decreased sharply. The increase in withdrawal speed intensified the evolution process. The stray grains formed in the remelted zone can be attributed to the twisting dendrite by the thermoelectric magnetic force. The distribution of more stray grains around the sample was caused by the circulation from thermoelectric magnetic convection at the macroscopic scale.

Development of a High-Efficiency Z-Form Selector for Single Crystal Blades and Corresponding Grain Selection Mechanism

A Comprehensive Understanding of Grain Selection in Spiral Grain Selector During Directional Solidification

Simulation And Experimental Studies On Grain Selection And Structure Design Of The Spiral Selector For Casting Single Crystal Ni-Based Superalloy

2-D Selector Simulation Studies On Grain Selection For Single Crystal Superalloy Of Cm247lc

Dependence of Microstructural Evolution on the Geometric Structure for Serviced DZ125 Turbine Blades

Using a Three-Dimensional Reduction Method in the High-Efficiency Grain Selector and Corresponding Grain Selection Mechanism

Grain Orientation Optimization Of Two-Dimensional Grain Selector During Directional Solidification Of Ni-Based Superalloys

Simulation and experimental studies on grain selection behavior of single crystal superalloy I. starter block

Grain Selection in a High-Efficiency 2D Grain Selector During Casting of Single-Crystal Superalloys

Production of Single-Crystal Seeds [001] from Nickel–Tungsten Alloys by Directional Crystallization

Modeling of Unidirectional Growth in a Single Crystal Turbine Blade Casting

Orientation Control for Nickel-Based Single Crystal Superalloys: Grain Selection Method Assisted by Directional Columnar Grains

Multi-scale Simulation of Single Crystal Hollow Turbine Blade Manufactured by Liquid Metal Cooling Process

Simulation and experimental studies on grain selection behavior of single crystal superalloy II. spiral part

Numerical Simulation and Experimental Grain Selection of DD6 Superalloy in Spiral Grain Selector by Directional Solidification

Temperature Evolution and Grain Defect Formation During Single Crystal Solidification of a Blade Cluster

Macro and micro numerical simulation of directional solidification of super alloy SX turbine blade

The recent progress in the design of structural strength and life assessment for aero-engine single crystal turbine blades

Simulation and Experimental Studies on Grain Selection Behavior of DD5 Single Crystal Superalloy

Numerical Simulation of Microstructure Evolution During Directional Solidification Process in Directional Solidified (DS) Turbine Blades

Formation and Evolution of Stray Grains on Remelted Interface in the Seed Crystal During the Directional Solidification of Single-Crystal Superalloys Assisted by Vertical Static Magnetic Field