Abstract:Long-term operation of oil and gas pipeline steels causes a significant worsening of their mechanical properties, especially characteristics of brittle fracture resistance. General regularities of in-service degradation of pipeline steels are analysed in the paper. Basing on these, two stages of pipeline steel degradation are distinguished: deformation aging and in-bulk steel dissipated microdamaging. Hydrogenation intensifies the damaging process due to hydrogen induced microcracking of steel and, in this way, facilitates its operational degradation. In-service damaging intensified by hydrogen can cause untypical mechanical behaviour of a metal: a) a decrease in strength and hardness is accompanied by reducing brittle fracture resistance; b) an increase in elongation simultaneously with a decrease in reduction in area. Some examples of the destructive role of hydrogen in-bulk material degradation are considered, when transported hydrocarbons serve as a source of hydrogen. It is shown that investigations of hydrogen behaviour in steels by hydrogen extraction and permeation methods provide valuable information for assessment of in-service dissipated damaging degree. In particular, a decrease of brittle fracture resistance is in a good agreement with hydrogen concentration in metal. Special attention is paid to the role of hydrogen in damaging rolled steels with texture during their operation. The main mechanism of microdamaging for textured steels is suggested to be the accumulation of hydrogen at the interface “elongated non-metallic inclusion–matrix” creating high pressure in defects with the following microdelamination along the rolling direction. This leads also to anisotropy of characteristics of brittle fracture resistance of rolled steels, which becomes more pronounced with operation time.

Mechanical Properties of Gas Main Steels after Long-Term Operation and Peculiarities of Their Fracture Surface Morphology

Analysis of the causes of fracture of the main gas pipeline

Assessment of Operational Degradation of Pipeline Steels

Methodology of hydrogen embrittlement study of long-term operated natural gas distribution pipeline steels caused by hydrogen transport

Peculiarities of Fatigue Crack Growth in Steel 17H1S after Long-Term Operations on a Gas Pipeline

Determining the influence of an artificial defect on the mechanical properties of a flexible pipeline material during a rupture test

Investigation of welded joints of long-term operated gas pipeline controllable rolled X70 steel

A Damage Mechanics based Evaluation of Dynamic Fracture Resistance in Gas Pipelines

DEVELOPMENT OF LOADING MODELS AND ANALYSIS OF THE STRESS-STRAIN STATE OF THE MAIN GAS PIPELINE WITH COMPOSITE LININGS

Evaluation of Failure Pressure for Gas Pipelines with Combined Defects

Experimental Evalua tion of the Mechanical Properties of the Metal of the Characteristic Zones of Typical Pipeline Elements

Role of hydrogen in operational degradation of pipeline steel

Evaluation of Hydrogen Embrittlement Risk of Long-Term Operated Gas Pipelines Made of 10G2BT Steel

Evaluating hydrogen embrittlement susceptibility of operated natural gas pipeline steel intended for hydrogen service

The Structural-Mechanical State of 12Kh1MF Steel of TPP Pipeline Bend after Long-Term Operation

Corrosion Degradation of Long-Term Operated Steel Sewer Pipes

The Analysis of the Influence of Various Factors on the Development of Stress Corrosion Defects in the Main Gas Pipeline Walls in the Conditions of the European Part of the Russian Federation

Structural features of crack formation during corrosion cracking

On the Issue of Improving Reliability of the Main Gas Pipelines

Fracture analysis of X80 welded joints with variable wall thickness and misalignment

Analysis of Mechanical Properties of Welded Joint Metal from TPP Steam Piping after Its Operational Degradation and Hydrogenation