Abstract:Several environmental challenges such as corrosion, low temperature, hydrogen-induced cracking (HIC), stress corrosion cracking (SCC), sulfide stress corrosion cracking (SSCC), and various other failure mechanisms contribute to the deterioration of the mechanical properties of pipeline steels, ultimately resulting in failure. In this review, diverse hydrogen attack sources, their possible failure mechanisms, and various strategies for their mitigation in different environments are explored. Optimizing the microstructure of pipeline steels can greatly improve their resistance to corrosion and cracking. This involves tailoring several microstructural parameters like the phase composition, dislocation density, crystallographic texture, grain size, grain boundary, and inclusions/precipitates, amongst others to the needs of the steel’s service environment. The evolving research landscape concerning the role of these microstructural parameters in corrosion, HIC, SCC, and other failure mechanisms was discussed in this study. It was established that crystallographic texture and grain boundary characteristics have roles to play in improving the SCC resistance of pipeline steels. However, the degree to which crystallographic texture, amidst other microstructural parameters, affects cracking is not yet established. For instance, the direct influence of crystallographic texture in the arrest of propagating cracks is still unclear and debated, while low-angle grain boundaries and CSL boundaries have been seen to arrest cracks in steels. It was also established that dislocation density, amongst other microstructural parameters, has a more profound effect on the HIC resistance of pipeline steels. Furthermore, this review examines the effect of hydrogen in pipeline welds. It investigates strategies to adapt existing pipelines' microstructure to meet the demands of operations in arctic environments. It was established that grain size, amongst other microstructural parameters, has a more profound effect on the mechanical properties of pipelines designated for cold applications. Finally, this review explores recent advancements in the transportation of gaseous hydrogen using existing pipeline steels (natural gas infrastructure). Ultimately, this study reinforces the importance of microstructure optimization in pipelines designated for different service environments, detailing the contribution of individual microstructural parameters to their overall performance and failure susceptibility in these environments.

Structural features of crack formation during corrosion cracking

Experimental and Numerical Analysis of the Impact of Corrosion on Pipeline Failure Pressure

The Analysis of the Influence of Various Factors on the Development of Stress Corrosion Defects in the Main Gas Pipeline Walls in the Conditions of the European Part of the Russian Federation

Causes of corrosion cracking of pipe metal and methods for their protection

A Damage Mechanics based Evaluation of Dynamic Fracture Resistance in Gas Pipelines

Stress corrosion cracking under extreme near-neutral GCC conditions, parametric and comparative study using phase field modeling

A Review of Factors Affecting SCC Initiation and Propagation in Pipeline Carbon Steels

Observations of Stress Corrosion Cracking in Pipeline Steel in Corrosive Seawater Environment Including Detailed Observation of the Crack Initiation Mechanism

Peridynamic Investigation of Stress Corrosion Cracking in Carbon Steel Pipes

Microstructural Effects in the Development of Near-Neutral pH Stress Corrosion Cracks in Pipelines

Stress Corrosion Crack Initiation Behavior for the X70 Pipeline Steel Beneath A Disbonded Coating

Analysis of the Physicochemical, Mechanical, and Electrochemical Parameters and Their Impact on the Internal and External SCC of Carbon Steel Pipelines

Effects of different microstructural parameters on the corrosion and cracking resistance of pipeline steels: A review

Analysis of the causes of fracture of the main gas pipeline

Surface Stress Analysis of Internally Corroded Pipes under External Pressure

The impact of residual technological stresses on the opening and stability of through cracks in pipeline elements

Mechanical Properties of Gas Main Steels after Long-Term Operation and Peculiarities of Their Fracture Surface Morphology

Sulfide Corrosion Cracking of Linepipe for Sour Gas Service

Failure Causes Analysis of Circumferential Cracking on Gathering Pipeline in M Oil and Gas Field

Stress Corrosion Cracking of X-70 Pipeline Steel in Near Neutral Ph Solution Subjected to Constant Load and Cyclic Load Testing

Corrosion assessment of ductile iron pipes using high-speed camera technique: Microstructural validation