Abstract:Synthesizing uniform microcrystals of high solid purity is desired for process efficiency and product consistency, but it is often challenging to achieve due to its high uniformity (e.g., the coefficient of variation in both crystal size and aspect ratio is less than 0.5) and mild reaction conditions (e.g., pH ∼ 7, room temperature). An example crystal is α-MnC2O4·2H2O, whose current precipitation synthesis often takes place in stirred-tank reactors and requires acidic pH, elevated temperatures, and/or extended hours. Crystal size uniformity control is also lacking. This study first demonstrates the feasibility of mild reaction conditions for synthesizing α-MnC2O4·2H2O in a stirred tank, at a stoichiometric ratio of 1:1 and an initial supersaturation of 7.5. This synthesis follows an indirect pathway, with a solid MnC2O4·3H2O (less-stable form) quickly precipitated first and then slowly transformed in slurry to α-MnC2O4·2H2O (conglomerates). Further, a new direct solution-precipitation pathway to obtaining pure α-MnC2O4·2H2O was discovered (without ever going through solid MnC2O4·3H2O and hour-long conversion) by replacing the “by-default” stirred tank/flask in the current synthesis with tubular slug flow at medium gas flow rates (e.g., 1.5–2.5 mL/min). With reduced gas flow rates in slug flow (from 10 to 1.5 mL/min), the induction time monotonically increases (from ∼50 to 137 s) and the mass portion of the undesired MnC2O4·3H2O among the reaction product solids also reduces (from ∼40 to 0%). Compared to a stirred tank at the same mild reaction conditions aimed at producing pure α-MnC2O4·2H2O, slug flow is able to reduce the reaction residence time from ∼30 to 0.3 h. The modular slug-flow design also allows not only incorporating production-cleaning cycles to prevent fouling but also scaling up the total volume using the same equipment. Throughout the continuous operation of 10 cycles (∼80 min) at medium gas flow rates, the product crystals from an initial supersaturation of 7.5 are consistently pure α-MnC2O4·2H2O, uniform in size (average length ∼14 μm, coefficient of variation less than 0.2), and are all in prism shape (average aspect ratio ∼1.4, coefficient of variation less than 0.25).

Mist Chemical Vapor Deposition Using Poorly Soluble Particles as Raw Material

Mist CVD Growth of ZnO-Based Thin Films and Nanostructures

Zno-based Thin Films Synthesized by Atmospheric Pressure Mist Chemical Vapor Deposition

Deposition of Y2O3 stabilized ZrO2 thin films from Zr(DPM)4 and Y(DPM)3 by aerosol-assisted MOCVD

Silicon Dioxide Deposition by Atmospheric Pressure and Low‐Temperature CVD Using TEOS and Ozone

Facile catalyst deposition using mists for fluidized-bed production of sub-millimeter-long carbon nanotubes

Mist chemical vapor deposition of Al1−xTixOy thin films and their application to a high dielectric material

Massive production of nanoparticles via mist reaction

A Novel Method for Growing α-Ga2O3 Films Using Mist-CVD Face-to-face Heating Plates

Fabrication of epitaxial V2O3 thin films on Al2O3 substrates via mist chemical vapor deposition

Numerical and Experimental Comparative Study of Metal-Organic Chemical Vapor Deposition of ZnO

Handling Nanoparticle Content in Nanocomposite Thin Films Deposited by Misty Plasma Processes through Controlled Flash Boiling Atomization

Chemical Vapor Deposition of MgAl2O4 Thin Films Using Different Mg−Al Alkoxides: Role of Precursor Chemistry

Guiding principles for the design of a chemical vapor deposition process for highly crystalline transition metal dichalcogenides

Aerosol And Plasma Assisted Chemical Vapor Deposition Process For Multicomponent Oxide Lao(0.8)Sro(0.2)Mno(3) Thin Film

C-Axis Aligned Crystalline InSnZnO Thin Film Using Mist Chemical Vapor Deposition and Deposition/Annealing Cyclic Method for Thin-Film Transistors Applications

Geometry of Chemical Beam Vapor Deposition System for Efficient Combinatorial Investigations of Thin Oxide Films: Deposited Film Properties versus Precursor Flow Simulations

Micro-cold Spray Deposition of YSZ Films from Ultrafine Powders Using a Pressure Relief Channel Nozzle

Numerical Study on Chemical Vapor Deposition of ZrC and Optimization of Deposition Uniformity with Flexible Flow Controller

Mist CVD deposited amorphous InSnZnO thin films with different nitrogen/oxygen ratios carrier gases and their applications to thin-film transistors

Direct Precipitation Pathway to Pure α-MnC 2 O 4 ·2H 2 O Using Slug Flow toward the Scalable Nonfouling Fast Synthesis of Uniform Microcrystals