Abstract:Herein, the adsorption of methyl orange (MO), a dangerous anionic dye, from an aqueous solution was investigated using a novel magnetic nanocomposite adsorbent. A nanocomposite entitled manganese chromium-layered double oxide/cobalt spinel ferrite, (MnCr)-LDO5wt.%/CoFe2O4, which links the interlayer structural characteristics of layered double oxides (LDOs) with the magnetic properties of spinel ferrites (SFs) was synthesized using the eco-friendly co-precipitation technique. Determination of structural parameters, crystallite size, and micro-strain was done using X-ray diffraction (XRD) analysis. Transmission electron microscopy (TEM) was used to determine grain shape and size. Surface analysis was performed using X-ray photoelectron spectroscopy (XPS) to identify elements and oxidation states present in the prepared nanocomposite. Vibrating sample magnetometer (VSM) was utilized to examine the magnetic characteristic. A comprehensive comparative study about the effectiveness and durability of CoFe2O4 and (MnCr)5wt.%/CoFe2O4 as nanoadsorbents for MO was conducted. Numerous variables, including contact time, MO concentration, adsorbent dosage, and pH were tested for their effects on the adsorption removal percentages. The findings showed that the maximum removal percentage was 86.1% for 25 ppm of MO was for 0.1 g/100 mL of (MnCr)-LDO5wt.%/CoFe2O4 at pH = 3. Investigations of isotherms and kinetics were conducted under batch conditions. The Langmuir isotherm matched the experimental data, for both nanoadsorbents, quite well due to the homogeneous distribution of active sites. Adsorption kinetics data were found to be compatible with intra-particle diffusion and pseudo-second order models for CoFe2O4 and (MnCr)5wt.%/CoFe2O4, respectively. A total of five adsorption-desorption cycles were performed to determine the prepared adsorbents' recyclable nature.

Preparation of porous spherical cuprous oxide and its adsorption properties

The Convenient Preparation of Porous CuO Via Copper Oxalate Precursor

Preparation of 26-facet Cu2O@Cu composite and its methyl orange adsorption behavior

Preparation of Manganese Oxides-Modified Diatomite and Its Adsorption Performance for Dyes

Preparation of Cuprous Oxide Particles of Different Crystallinity

Adsorptive Removal of Methylene Blue by CuO-acid Modified Sepiolite As Effective Adsorbent and Its Regeneration with High-Temperature Gas Stream.

Preparation of Micron Size Cuprous Oxide Powder from Acidic CuCl2 Etchant Waste Solution

MgAlFeCu Mixed Oxides for SO2 Removal Capacity: Influence of the Copper and Aluminum Incorporation Method

Synthesis and Photocatalytic Characterization of Porous Cuprous Oxide Octahedra

Fe_3O_4/Acrylate-based Magnetic Microparticles:Preparation and Adsorption Performance Toward Hg~(2+),Cu~(2+) and Ni~(2+)

The Ultrahigh Adsorption Capacity and Excellent Photocatalytic Degradation Activity of Mesoporous CuO with Novel Architecture

Preparation of Organically Functionalized Silica Gel As Adsorbent for Copper Ion Adsorption

Preparing conductive polymer-based adsorbent with better cupric ion adsorption efficiency by monomer precursor cross-linking method

A green and facile synthesis route of nanosize cupric oxide at room temperature

Preparation and characterization of a novel nanocomposite based on MnCr-layered double oxide and CoFe2O4 spinel ferrite for methyl orange adsorption

Preparation of hollow MgO nanosorbents via the templating method and study of their adsorption mechanism

Preparation of Fe-Mn bimetal oxide adsorbent and its adsorption characteristics of arsenic

A novel wet-chemical method of preparing highly monodispersed Cu2O nanoparticles

High Performance Adsorption of Orange II Dye Onto Modified Mussel Shell Powder

Fabrication of chitosan microspheres for efficient adsorption of methyl orange

Preparation of porous microspherical adsorbent via pine pollen stabilized O1/W/O2 double emulsion for high-efficient removal of cationic dyes