Abstract:The synthesis of a new resorbable porous bioactive silica-calcium phosphate composite (SCPC) that can be used as a tissue-engineering scaffold for bone regeneration is described. The effects of chemical composition and thermal treatment on crystallization and the mechanism of phase transformation in SCPC were evaluated. In the silica-rich samples, beta-rhenanite (beta-NaCaPO(4)) and alpha-cristobalite (SiO(2)) were the dominant phases after treatment at 800 degrees C. On the other hand, in the calcium phosphate-rich samples, calcium pyrophosphate (Ca(2)P(2)O(7)) was formed in addition to beta-rhenanite and alpha-cristobalaite. X-ray diffraction analyses showed a shift in the 2 theta value of the main peak(s) of all phases indicating the formation of solid solutions. Phase transformation reactions were accompanied by a loss of water molecules that contributed to the formation of pores in the size range 10-300 microm. All SCPC samples adsorbed a significantly higher quantity of serum protein than bioactive glass (p < 0.0001). In addition, the silica-rich SCPC adsorbed a significantly higher amount of serum protein than the calcium phosphate-rich samples (p < 0.003). While the crystallization of amorphous silica into L-quartz significantly inhibited serum protein adsorption, the transformation of L-quartz into alpha-cristobalite solid solution (ss) significantly enhanced protein adsorption. On the other hand, in conjunction with the transformation of brushite (CaHPO(4)) into pyro- and tri-calcium phosphates, there was a significant decrease in protein adsorption. However, as pyro- and tri-calcium phosphates transformed into beta-rhenanite, by thermal treatment, protein adsorption increased markedly. Critical-size bone defects grafted with silica-rich SCPC were filled with new bone and contained minimal residues of the graft material. Bone defects grafted with bioactive glass enhanced new bone formation, however, with very limited resorption. The enhanced resorption of SCPC in vivo correlates well with the higher rate of silica dissolution from SCPC than bioactive glass. The facilitated Si dissolution was associated with rapid bone regeneration in defects grafted with SCPC. The enhanced bioactivity properties of the SCPC are due to its chemical composition, modified crystalline structure, and high porosity. The new SCPC may be used for a wide variety of applications in the field of bone reconstruction including tissue-engineering scaffolds for cell and drug delivery.

Surface-Modified Diopside-Reinforced PCL Biopolymer Composites with Enhanced Interfacial Strength and Mechanical Properties for Orthopedic Applications

Silane Modified Diopside for Improved Interfacial Adhesion and Bioactivity of Composite Scaffolds

Synthesis and characterization of a photo-cross-linked bioactive polycaprolactone-based osteoconductive biocomposite

Designing of porous PMMA/diopside bone cement for non-load bearing applications

Experimental investigation of PCL‐based composite material fabricated using solvent‐cast 3D printing process

Synergistic fabrication of micro-nano bioactive ceramic-optimized polymer scaffolds for bone tissue engineering by in situ hydrothermal deposition and selective laser sintering

Development and characterization of PLA nanocomposites reinforced with bio-ceramic particles for orthognathic implants: Enhanced mechanical and biological properties

Experimental investigations on polydopamine coated poly lactic acid based biomaterial fabricated using 3D printing for orthopedic applications

Effect of Surface Modification on Impact Strength and Flexural Strength of Poly(lactic acid)/Silicon Carbide Nanocomposites

Bioceramic composites for orthopaedic applications: A comprehensive review of mechanical, biological, and microstructural properties

An Investigation of Siloxane Cross-linked Hydroxyapatite-Gelatin/Copolymer Composites for Potential Orthopedic Applications().

Optimization of Polydimethylsiloxane-Modified Composite Synthesis and Its Impact on Collagen Interactions: Perspectives for Biomedical Applications

Properties And Morphology Of Bioceramics/Poly(D,L-Lactide) Composites Modified By In Situ Compatibilizing Extrusion

Mechanism of Adhesion of Natural Polymer Coatings to Chemically Modified Siloxane Polymer

A New Strategy for PEEK-based Biocomposites to Achieve Porous Surface for Bioactivity and Adjustable Mechanical Properties for Orthopedic Stress Matching

Tuning of the Surface Biological Behavior of Poly(l-Lactide)-based Composites by the Incorporation of Polyelectrolyte Complexes for Bone Regeneration

Advanced bioceramic composite for bone tissue engineering: design principles and structure-bioactivity relationship

In vitro study of hydroxyapatite/polycaprolactone (HA/PCL) nanocomposite synthesized by an in situ sol-gel process

Strength, Toughness, and Reliability of a Porous Glass/biopolymer Composite Scaffold

Characterization on Modification and Biocompatibility of PCL Scaffold Prepared with Near-field Direct-writing Melt Electrospinning

Improvement of mechanical property of poly(ε-caprolactone)composite filled with nano-hydroxyapatite particles modified by KH570 silane coupling agents