Abstract:The main purpose of this research is to bolster mechanical properties of the parts, produced by an extrusion-based 3D printer, or fused deposition modeling machine, via increasing the content of continuous fiber yarn to its practical limit. In-melt continuous glass fiber yarn embedding was applied as a reliable and consistent method for simultaneous impregnation to produce continuous fiber-reinforced thermoplastic composites in the fused deposition modeling process. It is well known that the main weakness in the fused deposition modeling 3D printed products is their low strength compared to the manufactured ones by conventional methods such as injection molding and machining processes. This characteristic can be related to both inherent weakness of thermoplastic materials and poor adhesion between the deposited rasters and the layers. Although various attempts have been performed to tackle this issue, it is widely believed that using continuous fibers is the most effective method to serve this purpose if a reliable and consistent method is implemented. Since the mechanical properties of continuous fiber-reinforced composites directly depend on the content of fiber volume, maximizing the fiber content as well as producing an integrated part was assumed as the main objective. In this work, an analysis of various patterns of raster deposition was conducted, followed by the experiments and verification. The effective parameters on the fiber yarn volume, such as fiber yarn diameter, fiber yarn laying pattern, extrusion width, layer height, and flow percentage, were investigated and their optimal values were reported. The attained experimental results showed that, for polylactic acid-glass fiber yarn reinforced composite, with the extrusion width of 0.3 mm, the layer heights of 0.22 mm, flow percentage of 0.43, and the rectangular laying pattern, approximately 50% fiber-volume content can be achieved which resulted in tensile yield strength and modulus of 478 MPa and 29.4 GPa, respectively. There was an excellent agreement between these experimental results and predicted theoretically values by rule of mixture.

Impregnation modeling and preparation optimization of continuous glass fiber reinforced polylactic acid filament for 3D printing

Parametric Study on Manufacturing of Continuous Glass Fibers Reinforced Polylactic Acid (PLA) Filaments for 3D Printing

An investigation of preparation of continuous carbon fiber reinforced PLA prepreg filament

Process parameters and mechanical properties of continuous glass fiber reinforced composites-polylactic acid by fused deposition modeling

Fiber–matrix impregnation behavior during additive manufacturing of continuous carbon fiber reinforced polylactic acid composites

Preparation and Performance Index Test of Continuous Glass Fiber Reinforced Filament- Polylactic Acid for 3D Printer

Rapid prototyping of continuous carbon fiber reinforced polylactic acid composites by 3D printing

Effect of Process Parameters on Tensile Mechanical Properties of 3D Printing Continuous Carbon Fiber-Reinforced PLA Composites

Design and fabrication of high-performance 3D printed continuous flax fibre/PLA composites

Carbon Fiber-Reinforced PLA Composite for Fused Deposition Modeling 3D Printing

Experimental analysis of 3D printed continuous carbon/glass hybrid fiber reinforced PLA composites: Revealing synergistic mechanical properties and failure mechanisms

An innovative design approach in three-dimensional printing of continuous fiber–reinforced thermoplastic composites via fused deposition modeling process: In-melt simultaneous impregnation

Improving mechanical properties of continuous fiber-reinforced thermoplastic composites produced by FDM 3D printer

Preparation of short CF/GF reinforced PEEK composite filaments and their comprehensive properties evaluation for FDM-3D printing

Preparation and Process Parameter Optimization of Continuous Carbon Fiber-Reinforced Polycarbonate Prepreg Filament

The fabrication of long carbon fiber reinforced polylactic acid composites via fused deposition modelling: Experimental analysis and machine learning

Process optimization of continuous flax fiber/polylactic acid prepreg filaments toward high performance 3D‐printed composites

Polylactide Composites Reinforced with Pre-Impregnated Natural Fibre and Continuous Cellulose Yarns for 3D Printing Applications

Process-induced Property Loss of Prepreg Filaments with Continuous Fiber Content of 65 Vol% Suitable for Direct 3D Printing

Process-dependent Multiscale Modeling for 3D Printing of Continuous Fiber-reinforced Composites

Manufacturing and 3D printing of continuous carbon fiber prepreg filament