Anionic defect-enriched ZnMn2O4 nanorods with boosting pseudocapacitance for high-efficient and durable Li/Na storage

Shikun Cheng,Qiang Ru,Yuqing Gao,Minhui Zhen,Fuming Chen,Li Wei,Francis Chi-Chung Ling

DOI: https://doi.org/10.1016/j.cej.2020.126133

IF: 15.1

2021-02-01

Chemical Engineering Journal

Abstract:<p>Anionic defect (oxygen vacancies)-enriched ZnMn₂O₄ nanorods (OZMO) were manufactured through a facile coprecipitation/chemical reduction route. The synergetic mechanism of rich oxygen vacancies, abundant mesopores, and prominent pseudocapacitance endows the OZMO nanorods with long-term chemical durability for high-efficient lithium/sodium storage. When evaluated as anodes for lithium-ion batteries, the OZMO electrode exhibits a conspicuous reversible capacity of 1566.7 mAh g⁻¹ after 50 cycles at 0.1 A g⁻¹, remarkable cyclability with 380.1 mAh g⁻¹ after 1000 cycles at an ultrahigh current density of 10 A g⁻¹, as well as a good environmental adaptation with 568.6 and 811.4 mAh g⁻¹ at −5 °C and 55 °C. For sodium-ion batteries, the OZMO electrode delivers a stable discharge capacity of 110.8 mAh g⁻¹ after 1000 cycles at a large current density of 1 A g⁻¹. The UV–Vis diffusive reflectance spectrum shows that the OZMO sample has a narrow bandgap, thus improving the electrical conductivity. Moreover, this strategy may increase the active sites, which provides a large electrolyte/electrode contact area and shortens the diffusion distance for both ions and electrons, thereby buffering the volume variation originated from the repeated Li⁺/Na⁺ intercalation/deintercalation process.</p>

engineering, chemical, environmental