Improved energy-storage and charge–discharge properties achieved in NaNbO3-Bi(Mg0.5Zr0.5)O3 ceramics

Hongjuan Hao,Hongbin Pu,Dingze Lu,Min Zhou,Xin Zhang,Pengfei Cheng

DOI: https://doi.org/10.1007/s10854-024-13580-7

2024-09-28

Journal of Materials Science Materials in Electronics

Abstract:Herein, the energy-storage performance of NaNbO 3 -based lead-free ceramics has been successfully reinforced by introducing Bi(Mg 0.5 Zr 0.5 )O 3 to improve the breakdown strength (BDS) and suppress the remnant polarization ( P r ). A superior discharge energy density ( W d ) of 3.01 J cm −3 and an outstanding energy efficiency ( η ) of 90.2%, accompanied with high thermal stability of energy-storage performance ranging from 30 °C to 150 °C, have been concurrently recorded in 0.88NaNbO 3 -0.12Bi(Mg 0.5 Zr 0.5 )O 3 ceramic at 320 kV cm −1 . The results show that the introduction of Bi(Mg 0.5 Zr 0.5 )O 3 can enhance BDS due to its considerable insulation, which is confirmed by the calculation of the band structure and the projected density of states. In addition, the remarkable current density ( C D ) of 644.51 A cm −2 , preeminent power density ( P D ) of 38.68 MW·cm −3 and transient energy release times ( t 0.9 ) of 41.2 ns were also obtained in 0.88NaNbO 3 -0.12Bi(Mg 0.5 Zr 0.5 )O 3 ceramic. Therefore, this study can significantly contribute to the application of NaNbO 3 -based ferroelectrics in advanced pulsed power systems.

engineering, electrical & electronic,materials science, multidisciplinary,physics, condensed matter, applied