Influence of deformation temperature on flow stress and dynamic metallurgical phenomena in Al–5.81Zn–1.65Mg alloy subjected to thermomechanical processing
Hyung-Won Park,Hyeon-Woo Park,Yuki Shimomura,Yun-Soo Lee,Hyeon-Woo Son,Sungho Jeon,Tomohiro Hata,Jun Yanagimoto
DOI: https://doi.org/10.1016/j.mtcomm.2024.111208
IF: 3.8
2024-12-06
Materials Today Communications
Abstract:To advance the T5 treatment process for Al–5.81Zn–1.65Mg alloys, this study explored the influence of deformation temperature on the solution temperature, ultrafine grain (UFG) formation via dynamic recrystallization (DRX), and strain-induced dynamic precipitation (SIDP) during thermomechanical processing at 300–500 °C, with a 70 % reduction and a strain rate of 1 s −1 . The flow curve exhibited pronounced work hardening (WH) at 300–350 °C, whereas a dynamic recovery-type flow curve was observed at 450–500 °C. As the temperature increased from 300 to 500 °C, the 1st WH rates ( ε =0.2–0.4) were 55, 37.5, 20, 8.5, and 10 MPa, respectively. Larger DRX grains were formed at higher temperatures. The DRX rate ranged 20 %–30 % at 300–400 °C and increased to 60 % at 500 °C. The texture gradually transitioned from Goss {011} to brass {110} with an increase in the deformation temperature from 300 to 500 °C. Discontinuous DRX occurred mainly near the grain boundaries and precipitates at 300–400 °C, shifting to continuous DRX at temperatures ranging from 400 to 500 °C. At 300 and 400 °C, larger precipitates (10–50 nm) and smaller ones (<10 nm) were observed within grains and along boundaries. Precipitates at 300 °C were larger and denser than those at 400 °C, with η', and T' phases formed through SIDP. For this alloy, considering the formation of UFG and ensuring sufficient solubility, the appropriate deformation temperature range was 400–500 °C.
materials science, multidisciplinary