Effects of Carbon/Glass Nonwoven Interleaving veils and their Areal Density on Opening and Shearing Mode Interlaminar Fracture Toughness of Glass Epoxy Composites

Vinayak S. Uppin,P.S. Shivakumar Gouda,I. Sridhar,M.A. Umarfarooq,Abhilash Edacherian

DOI: https://doi.org/10.1016/j.tafmec.2024.104292

IF: 4.374

2024-01-23

Theoretical and Applied Fracture Mechanics

Abstract:The study explores the impact of Carbon and Glass nonwoven interleaving veils with varying areal density on delamination resistance in unidirectional (UD) Glass epoxy composites under Opening (Mode-I) and Shearing (Mode-II) mode loadings. Commercially available non-woven Carbon and Glass interleaves with areal densities of 15, 20, 25, and 30 g/m 2 were used to manufacture the interleaved Glass epoxy laminates. Double Cantilever Beam (DCB) and End Notch Flexural (ENF) specimens were used to determine the mode-I and mode-II fracture energies. The results reveal that, during mode-I initiation, interleaved laminates exhibit a lower interlaminar fracture toughness (IFT) except for the Carbon fiber interleaved laminates of areal density 30 g/m 2 . However, during propagation, all veils interleaved laminates presented significant improvement in IFT ranging from 5 to 25% accompanied by substantial fiber bridging. In case of mode-II test, the laminates with Carbon and Glass veils exhibit enhanced IFT (60-182%) with increasing areal density compared with the non-interleaved Glass laminates. Optical and scanning electron micrographs (SEM) provide evidence of fracture mechanisms involved in the interleaved and non-interleaved composite laminates.

engineering, mechanical,mechanics