Microstructure and properties of TiAl-4822 alloy subject to the solid-state treatment with pulsed magnetic field
G.R. Li,B.W. Zhao,H.M. Wang,Z.J. Ji,X.F. Ding,H. Nan,J.J. Zhang,T.T. Wu,S.M. Chen
DOI: https://doi.org/10.1016/j.matchar.2024.113919
IF: 4.537
2024-04-17
Materials Characterization
Abstract:The limited plasticity of γ-TiAl-based alloys presents a significant challenge in their application for aerospace components. In this study, the as-cast TiAl-4822 (Ti-48Al-2Nb-2Cr) alloy was subjected to magnetic field treatment at varying levels of magnetic induction intensity. The pulsed magnetic field induces magnetic stress and thermal effects on the microstructure of grains and dislocations, resulting in an increased lamellar spacing, reduced lamellar thickness, equiaxed γ precipitation, abundant grain boundaries, a high dislocation density, finer grains, and prominent orientation characteristics. The changes in microstructure and properties of 1 T and 2 T specimens are not readily discernible; however, a significant grain refinement is observed in the case of 3 T and 4 T specimens. Additionally, there is an increase in dislocation density evident, accompanied by an enhancement in lamellar structure as well as the emergence of equiaxial γ-TiAl phase. The elongation and tensile strength of the optimized 4 T specimens have simultaneously increased by 31.3% and 11.57%, resulting in values of 0.84% and 261.61 MPa, respectively, compared to those of the untreated alloy.
materials science, multidisciplinary,metallurgy & metallurgical engineering, characterization & testing