Abstract:With the rapid growth of shield-discharged soil (SDS), there is an increasing demand for effective recycling and transformation methods. This study aims to develop an alkali-activated controlled low-strength material (CLSM) by utilizing ground granulated blast furnace slag (GGBFS) and fly ash (FA) as precursors, SDS as fine aggregate, and sodium hydroxide (NaOH) solution as an activator. The Box-Behnken design (BBD) within the response surface methodology (RSM) framework was employed, considering liquid-to-solid ratio, alkali equivalent, aggregate-to-binder ratio, and foam agent content (FC) in SDS as key factors. Regression models were constructed to analyze the effects of these factors on flowability, bleeding rate, setting time, compressive strength, elastic modulus, and water absorption. The results confirmed the effectiveness of RSM in determining optimal conditions for material performance. In addition, microscopic analyses were conducted to explore hydration products, microstructural characteristics, and pore distribution. The findings revealed that the fresh density of the CLSM ranged from 1460 to 1740 kg/m3, classifying it as a low-density material. The 28-day compressive strength varied from 1.837 to 7.884 MPa, while the setting time ranged between 1.2 and 5.6 hours. These properties comply with the ACI 229 standard and are suitable for practical applications. Interestingly, when the aggregate-to-binder (A/B) ratio was between 0.2 and 0.4, increasing the ratio did not lead to a consistent reduction in mechanical properties. Instead, the properties initially decreased and then improved. Moreover, an increase in foam agent content (FC) extended the setting time and reduced mechanical strength. The correlation coefficients of all models exceeded 0.98, with a coefficient of variation below 10 % and a signal-to-noise ratio greater than 4, demonstrating strong reliability and accuracy of the models. Additionally, the average relative error between predicted and experimental values in six scenarios was under 6 %, validating the feasibility of optimizing the design of alkali-activated CLSM using RSM. The formation of Ca(OH)2 crystals facilitates early strength development, resulting in final cementitious materials reticular, fibrous C-S-H, C-A-H, and other gel-like hydration products. Calcium promotes the formation of gels such as C-S-H, shortening the setting time and enhancing microstructural density. This study provides valuable insights for optimizing the design of alkali-activated CLSM containing SDS, thereby expanding methods for utilizing construction and demolition waste.

Synthesis of CaLiAl-LDHs and its optimization on the properties and chloride binding capacity of eco-friendly marine cement-based repair materials

Understanding the Role of Calcium Silicate Slag in Sodium Carbonate-Activated Green Materials: Influence on Kinetics, Strength, and Efflorescence

Effects of Cyclic Seawater Exposure on the Mechanical Performance and Chloride Penetration of Calcium Sulfoaluminate Concrete

Mechanical Performance and Chloride Penetration of Calcium Sulfoaluminate Concrete in Marine Tidal Zone

Study on the chloride ion binding rate of sulfoaluminate cement mortars containing different mineral admixtures

A novel ultrasonic method to exfoliate CLDH toward improving mechanical and chloride binding properties of cementitious composites

Investigation on chloride resistance of high-volume slag low-carbon cement-based materials with crystalline admixture under seawater

Chloride Binding in Cement Paste with Calcined Mg-Al-CO3 LDH (CLDH) under Different Conditions

Efficient Utilization of Waste Marine Clay for Fine Aggregate to Develop Sustainable and Cost-Effective Strain-Hardening Cement-Based Composites

Chloride binding behavior of synthesized reaction products in alkali-activated slag

Insights into the effect mechanism of nano LiAl-LDHs on the early hydration of sulphoaluminate cement-based materials

Ca-Al LDH hybrid self-healing microcapsules for corrosion protection

Influence of Different Lithium Compounds on Hydration and Mechanical Properties of Calcium Sulfoaluminate Cement

Drying–Wetting Correlation Analysis of Chloride Transport Behavior and Mechanism in Calcium Sulphoaluminate Cement Concrete

Properties of calcium sulfoaluminate cement-based grouting materials with LiAl-layered double hydroxides slurries

Improved chloride binding capacity and corrosion protection of cement-based materials by incorporating alumina nano particles

Optimization and characterization of GGBFS-FA based alkali-activated CLSM containing Shield-discharged soil using Box-Behnken response surface design method

Mechanical properties and hydration of ultra-high-performance seawater sea-sand concrete (UHPSSC) with limestone calcined clay cement (LC3)

Effect of LDH on the dissolution and adsorption behaviors of sulfate in Portland cement early hydration process

Characterization and adaptability of layered double hydroxides in cement paste

Chloride binding capacity of LDHs with various divalent cations and divalent to trivalent cation ratios in different solutions