Investigation of structure and cycling performance of Nb5+ doped high‐nickel ternary cathode materials

Feng Tian,Yongzheng Zhang,Zhongzhu Liu,Robson de Souza Monteiro,Rogerio Marques Ribas,Peng Gao,Yongming Zhu,Hailong Yu,Liubin Ben,Xuejie Huang

DOI: https://doi.org/10.1016/j.ssi.2020.115520

IF: 3.699

2021-01-01

Solid State Ionics

Abstract:<p>Nickel-rich layered LiNi_0.8Co_0.1Mn_0.1O₂ is a promising cathode material due to its high specific capacity. However, commercial application of this material is impeded by its rapid capacity degradation associated with structural instability. In this work, 0.5–2 mol% Nb⁵⁺ doped LiNi_0.8Co_0.1Mn_0.1O₂ cathode material is prepared by heat treatment of a mixture of stoichiometric amounts of nano-sized Nb₂O₅ powders, co-precipitated Ni_xMn_1-x(OH)₂ precursors, and LiOH·H₂O. The results show that Nb⁵⁺ doping significantly improves the cycling properties of LiNi_0.8Co_0.1Mn_0.1O₂ cathode material and that the optimal Nb⁵⁺ content in the structure is 1 mol%. Under a voltage range of 2.75–4.3 V, 1 mol% Nb⁵⁺ doped LiNi_0.8Co_0.1Mn_0.1O₂ cathode material shows an initial discharge capacity of 180.2 mAh/g at 0.1C, with a capacity retention of 96.9% for subsequent 300 cycles at 1C at room temperature. In contrast, bare LiNi_0.8Co_0.1Mn_0.1O₂ shows a capacity retention of only ~79.8% under the same conditions, with an initial specific discharge capacity of 184.9 mAh/g. The improvement in cycling performance is attributed to stabilization of the layered structure by Nb⁵⁺, mitigated migration of Ni²⁺ to the Li layer, improved lithium diffusion kinetics and reduced lattice expansion/shrinkage during cycling. Stabilization of the layered structure by Nb⁵⁺ doping is further reflected by the observation of fewer cracks in cathode electrodes after prolonged cycling.</p>

chemistry, physical,physics, condensed matter