Structure and microwave dielectric properties of CaZr0.99−x(Zn1/3Nb2/3)xTi0.01O3 (0 ≤ x ≤ 0.2) microwave dielectric ceramics
Qiang Ren,Qinglin Liu,Haojie Dai,Zhongqing Tian,Chunyan Zhang,Fei Wang,Fancheng Meng,Huixing Lin
DOI: https://doi.org/10.1007/s10854-024-13927-0
2024-12-01
Journal of Materials Science Materials in Electronics
Abstract:The CaZr 0.990− x (Zn 1/3 Nb 2/3 ) x Ti 0.01 O 3 (CZT- x ZN, x = 0, 0.025, 0.05, 0.1, 0.2 mol) ceramics were successfully prepared by substituting (Zn 1/3 Nb 2/3 ) 4+ for Zr 4+ . With the increase of x , the crystals are orthorhombic structure. And, the cell volume and lattice constant decrease with the increase of x . Based on the SEM results, the grains become uneven and fine with the increase of x . Based on the Raman, it is found that the 1:2 ordered structure degree increases. With the increase of x , the dielectric constant ( ε r ) increases, the Q × f values first increase and then decreases. the temperature coefficient of resonance ( τ f ) is in inverse proportion to tolerance factor ( t ). When the sintering temperature is 1520°C, the microwave dielectric properties of the CZT-0.025ZN and CZT-0.05ZN ceramics are excellent, which are ε r = 30.6, Q × f = 37,360 GHz, τ f = 1.5 ppm/°C and ε r = 31.6, Q × f = 36280 GHz, τ f = 1 ppm/°C, respectively.
engineering, electrical & electronic,materials science, multidisciplinary,physics, condensed matter, applied