Pressureless-sintered boron nitride nanosheets/glass composite ceramics for excellent mechanical, dielectric and thermo-conductive performances
Wei Qiao,Jingwen Yang,Jiaxiao Qiao,Hejun Gao,Zexia Li,Peng Wang,Chaochao Cao,Jun Zhang,Yanming Xue,Chengchun Tang
DOI: https://doi.org/10.1016/j.jeurceramsoc.2023.02.072
IF: 5.7
2023-03-03
Journal of the European Ceramic Society
Abstract:Because they have a high application potential in the thermal management of insulation environments, the high-quality hexagonal boron nitride (h-BN)-based multiphase ceramics have been highly desired. However, so far, their synthesis is still full of challenges. Here, a kind of boron nitride nanosheets (BNNSs)/glass (GS) composite ceramics was prepared by a pressureless sintering method at a lower temperature of 900 °C. Due to a tightly bonded interaction between BNNSs and GS, the formed BNNSs/GS ceramics exhibit excellent multifunction performance. They have a maximum compressive strength range of 19 ~ 64 MPa and Vickers hardness ranging from 50 to 179 HV. For the BNNSs/GS ceramics with BNNS's filling fraction of 90 wt.%, their side-surface TC values are 12.01 ± 0.18 W m -1 K -1 at 25 °C and 13.64 ± 0.37 W m -1 K -1 at 300 °C, respectively. In the ultra-high frequency range of 26.5 ~ 40 GHz, the dielectric constant of the BNNSs/GS ceramics are primarily between 2 and 3, and the corresponding loss tangent value is < 0.3. In addition, based on the remarkable integrity of their structure, these BNNSs/GS ceramics exhibit outstanding thermal-shock stability and prominent thermal management capacity during lots of heating/cooling-testing cycles. Therefore, we believe this kind of BNNSs/GS ceramic system will have great application potential in the new-generation thermal management and/or insulation packaging fields.
materials science, ceramics