Crosslinking using particulate crosslinker in polymer latex film-coating process for controlled-release fertilizer

Shaolei Zhao,Jiuren Xie,Zhenkang Liu,Rui Tan,Ling Yang,Ting-Jie Wang

DOI: https://doi.org/10.1016/j.colsurfa.2024.134448

IF: 5.518

2024-06-03

Colloids and Surfaces A Physicochemical and Engineering Aspects

Abstract:Fertilizing controlled-release fertilizer is apt to keep a reasonable concentration of nutrient in soil and increase the efficiency of fertilizer utilization. The production of film-coated controlled-release fertilizer using polymer latex is a green process. However, the release period is usually short because the film crosslinking density is low during the fast film formation of the dynamic granule coating. In this study, numerous epoxy groups were grafted onto the nanoparticle surface of single-particle-dispersed silica to prepare particulate crosslinker with abundant crosslinking sites. The epoxy groups on the surface of the particulate crosslinker reacted with the carboxyl groups on the surface of the styrene-acrylate latex particles during film formation, enhancing film crosslinking. With the addition of the particulate crosslinker, the polymer latex was used to coat urea granules in a fluidized bed via spray coating at a low coating content of 4 wt%. The release period of film-coated urea granules with an enhanced crosslinking film reached 40 d, which was five times longer than that in the absence of particulate crosslinker.

chemistry, physical