Ar ion irradiation effect on the soft magnetic performance of Fe-based amorphous alloys
Qiang Luo,Xindu Fan,Baowei Miao,Baolong Shen,Jun Shen
DOI: https://doi.org/10.1016/j.jmmm.2020.166962
IF: 3.097
2020-10-01
Journal of Magnetism and Magnetic Materials
Abstract:<p>We investigate the effect of Ar ion irradiation on the microstructure and soft magnetic behaviors of Fe<sub>80</sub>Co<sub>x</sub>B<sub>14-x</sub>Si<sub>2</sub>P<sub>3</sub>Cu<sub>1</sub> (x=0, 2, 4) amorphous alloys by using X-ray diffraction (XRD), differential scanning calorimetry (DSC) and soft magnetic performance analysis. With increasing Co content, the alloy shows decreasing radiation resistance, i.e., more degree of nanocrystallization induced by irradiation. It is found that after irradiation with fluence of ∼9.0×10<sup>14</sup>, the coercivity is reduced from 7.6 A/m to 7.0 A/m, but increases again with further increase of irradiation fluence due to the formation of larger nanosized α-Fe(Co) grains. And with increasing irradiation fluence, the saturation magnetic flux density first decreases slightly from 1.65 T to 1.64 T, and then increases gradually to 1.68 T. Further, the core loss and effective magnetic conductivity were tuned obviously by irradiation, which has been discussed in term of stress relaxation and nanocrystallization.</p>
materials science, multidisciplinary,physics, condensed matter