Abstract:Successful preparation of photopolymerizable ceramic slurries using non-oxide ceramics and their 3D printing is highly challenging as the ceramic powders often possess high UV-light absorbance. Even though pre-oxidation of the powders could improve the slurry printability, the residual oxygen element in the material would eventually deteriorate the material purity and performance. In this study, a separated redox route (pre-oxidation, 3D printing and carbothermal reduction) was proposed to overcome these challenges. SiC ceramic powder was pre-oxidized into SiC@SiO2 core-shell form to lower the UV-light absorbance. It was found that the ultraviolet (UV) light absorbance value of SiC powder at 405 nm decreased 20% from 0.357 to 0.284 after pre-oxidation process. The UV-light penetration depth of SiC@SiO2 ceramic slurries at 40 similar to 55 vol% solid loading ranging from 14.81 to 12.82 mu m, which surpassed two times that for 40 vol% raw SiC ceramic slurry. Different-shaped structures of SiC@SiO2/resin green ceramic bodies were successfully fabricated by vat photopolymerization 3D printing. The oxygen element resided was then eliminated by carbothermal reduction to avoid detriment of SiO2 to the mechanical performance of the SiC ceramics. Phenolic epoxy acrylate resin with 14 wt% pyrolytic carbon (PyC) yield was chosen as the carbon source and thus the SiC@SiO2/resin green body pyrolyzed into SiC@SiO2/PyC ceramics after 1200 degrees C. It was found that after the heating temperature was further raised to 1600 degrees C, most of the pre-introduced SiO2 shells on the surface of SiC particles were in situ transformed into SiC nanowires through carbothermal reduction reaction between SiO2 and PyC, and the content of oxygen element in the ceramic matrix sharply dropped from 20.21% to 2.08%. The results demonstrated that through the proposed redox route, the photopolymerization-related issues including high UV-light absorbance and pre-oxidation-induced impurity for 3D printing of SiC ceramic slurries can be tackled. Finally, high purity porous SiCnw/SiC ceramic components with different structures were produced. This study provides a promising route for the preparation and 3D printing of photopolymerization ceramic slurries using non-oxide ceramics possessing high UV-light absorbance.

Highly Efficient Consolidation of Mesoporous Silica Microstructures Using Photonic Curing

Solventless 3D Printed High-Temperature Resistant Cyclosiloxane-Containing Resin for Low-Shrinkage Ceramization and Nano-Functional Composite Development

Nanoscale Features of Zeolite Fillers Enhance the Depth of Cure, Optical Properties, and Mechanical Properties of 3D-Printed Polymer Composite Structures

Optimization of Curing Behavior of Si3N4 UV Resin for Photopolymerization 3D Printing

Synthesis of Silicon and Germanium Oxide Nanostructures via Photonic Curing; a Facile Approach to Scale Up Fabrication

Photopolymerization of ceramic/zeolite reinforced photopolymers: Towards 3D/4D printing and gas adsorption applications

Solmers: Versatile hybrid resins for nanometric 3D printing of silica-based photonic components

PDMS Curing Inhibition on 3D-Printed Molds: Why? Also, How to Avoid It?

Printing of In Situ Functionalized Mesoporous Silica with Digital Light Processing for Combinatorial Sensing

Thermal Effects in Single-Point Curing Process for Pulsed Infrared Laser-Assisted 3D Printing of Optics

3D Printing and in Situ Transformation of SiCnw/SiC Structures

Digital Light Processing 3D‐Printed Silica Aerogel and as a Versatile Host Framework for High‐Performance Functional Nanocomposites

Silica‐Rich Sol‐Gel Ink for Two‐Photon Direct Laser Writing of Microscale Structures and Optical Elements

3D Inkjet Printing of Biomaterials with Solvent‐Free, Thiol‐Yne‐Based Photocurable Inks

A Comparative Study on 3D Printed Silicone-Epoxy/acrylate Hybrid Polymers Via Pure Photopolymerization and Dual-Curing Mechanisms

Additive manufacturing of ceramics from preceramic polymers: A versatile stereolithographic approach assisted by thiol-ene click chemistry

3D Printing of Ordered Mesoporous Silica Complex Structures

Optimizing photocuring properties of ceramic slurry for 3D printing of ceramic membranes

Preparation and optimization of silicon nitride slurries for digital light processing

Photopolymerization of Zeolite Filler‐Based Composites for Potential 3D Printing Application and Gas Adsorption Applications

Laser‐Assisted Direct Ink Writing for High‐Fidelity Fabrication of Elastomeric Complex Structures