Preparation of Silver-Coated Silica Microspheres with High Electrical Conductivity Through Pyrogallol-Fe(Ш) Coordinated Surface Functionalization

Bo Zhang,Xue Li,Wencai Wang,Mingzheng Hao,Ming Tian,Hua Zou,Liqun Zhang
DOI: https://doi.org/10.1007/s10904-020-01658-8
IF: 3.518
2020-07-08
Journal of Inorganic and Organometallic Polymers and Materials
Abstract:In this study, we report a facile method to fabricate silica-silver (SiO<sub>2</sub>/ PG-Fe<sup>3+</sup>/Ag) core–shell composite microspheres. The surface of SiO<sub>2</sub> microspheres is functionalized with pyrogallol-ferric ions (PG-Fe<sup>3+</sup>) complexes, then Ag ions are reduced to Ag nanoparticles in situ onto the surface of SiO<sub>2</sub> microspheres by electroless plating process. The Ag nanoparticles were uniformly coated on the surface of the SiO<sub>2</sub> microspheres and formed a distinctive layer, which was confirmed by scanning electron microscopy characterization. The chemical compositions and microstructures of the microspheres were investigated by X-ray photoelectron spectroscopy and X-ray diffraction, respectively. The electrical conductivity of the prepared SiO<sub>2</sub>/ PG-Fe<sup>3+</sup>/Ag core–shell microspheres was about 1000 S/cm. When the microspheres were filled in methyl vinyl silicone rubber (MVQ), the obtained composites showed good mechanical and electrical properties, indicating their potential applications as conductive and electromagnetic shielding materials.
polymer science
What problem does this paper attempt to address?
The paper primarily addresses the issue of how to prepare silver-coated silica (SiO2/PG-Fe3+/Ag) core-shell microspheres with high conductivity and explores the potential applications of these microspheres in the fields of conductive and electromagnetic shielding materials. Specifically, the researchers achieved this goal through the following steps: 1. **Surface Functionalization**: First, the silica microspheres were surface-functionalized using a catechol-iron ion (PG-Fe3+) complex to enhance their surface activity. 2. **Silver Nanoparticle Deposition**: Next, silver nanoparticles were deposited on the surface of the silica microspheres via a chemical reduction method, forming a uniform silver layer. 3. **Performance Testing**: Finally, the prepared SiO2/PG-Fe3+/Ag microspheres were mixed with methyl vinyl silicone rubber (MVQ) to create a composite material with good mechanical properties and conductivity. This method not only simplifies the preparation process but also improves the cost-effectiveness of the material. The prepared SiO2/PG-Fe3+/Ag microspheres exhibit a conductivity as high as 1000 S/cm, and when filled into MVQ, the resulting composite material shows good mechanical properties and conductivity (142 S/cm), indicating their potential application value in conductive and electromagnetic shielding materials.