Abstract:Intermetallic compounds are emerging as promising oxygen reduction reaction (ORR) catalysts for fuel cells due to their typically higher activity and durability compared to disordered alloys. However, the preparation of intermetallic catalysts often requires high-temperature annealing, which unfortunately leads to adverse sintering of the metal nanoparticles. Herein, we develop a scalable site-selective sulfur anchoring strategy that effectively suppresses alloy sintering, ensuring the formation of efficient intermetallic electrocatalysts with small sizes and high ordering degrees. The alloy-support interactions are precisely modulated by selectively modifying the alloy-support interfaces with oxidized sulfur species, thus simultaneously blocking both the nanoparticle migration and Oswald ripening pathways for sintering. Using this strategy, sub-5 nm PtCo intermetallic electrocatalysts enclosed by two atomic layers of Pt shells have been successfully prepared even at a metal loading higher than 30 wt%. The intermetallic catalysts exhibit excellent ORR performances in both rotating disk electrode and membrane electrode assembly conditions with a mass activity of 1.28 A mgPt-1 at 0.9 V (vs. RHE) and a power density of 1.0 W cm-2 at a current density of 1.5 A cm-2. The improved performances result from the enhanced Pt-Co electronic interactions and compressive surface strain generated by the highly ordering structure, while the atomic Pt shells prevent the dissolution of Co under highly acidic conditions. This work provides new insights to inhibit the sintering of nanoalloys and would promote the scalable synthesis and applications of platinum-based intermetallic catalysts.

Alloying Matters for Ordering: Synthesis of Highly Ordered PtCo Intermetallic Catalysts for Fuel Cells

Local Coordination and Ordering Engineering to Design Efficient Core-Shell Oxygen Reduction Catalysts

Phase Diagrams Guide Synthesis of Highly Ordered Intermetallic Electrocatalysts: Separating Alloying and Ordering Stages

Intermetallic PtFe Electrocatalysts for the Oxygen Reduction Reaction: Ordering Degree-Dependent Performance.

Rational Development of Structurally Ordered Platinum Ternary Intermetallic Electrocatalysts for Oxygen Reduction Reaction

Oxygen Vacancy-Mediated Synthesis of Inter-Atomically Ordered Ultrafine Pt-Alloy Nanoparticles for Enhanced Fuel Cell Performance

Ordered Pt 3 Co Catalysts Derived from ZIF-67 Templated Carbon for Oxygen Reduction Reaction

Pt-Based Intermetallic Compound Catalysts for the Oxygen Reduction Reaction: Structural Control at the Atomic Scale to Achieve a Win–Win Situation Between Catalytic Activity and Stability

Seed‐Mediated Synthesis of High Loading PtCo Intermetallic Compounds Enhanced Catalytic Efficacy and Long‐Term Stability for Oxygen Reduction Reaction

Breaking Trade-off Between Particle Size and Ordering Degree of Intermetallic Catalysts for Fuel Cells

Ordered Intermetallic PtCu Catalysts Made from Pt@Cu Core/Shell Structures for Oxygen Reduction Reaction

Site-selective sulfur anchoring produces sintering-resistant intermetallic ORR electrocatalysts for membrane electrode assemblies

Structurally Ordered Low‐Pt Intermetallic Electrocatalysts Toward Durably High Oxygen Reduction Reaction Activity

Unveiling enhanced oxygen reduction activity in PtCo bimetallic solid solutions through controlled crystal strain

Highly stable and active catalyst in fuel cells through surface atomic ordering

Ordering‐dependent hydrogen evolution and oxygen reduction electrocatalysis of high‐entropy intermetallic Pt4FeCoCuNi

PtCoFe Intermetallic Alloy Catalyst Derived from PtFe@CoO with High Stability for Oxygen Reduction Reaction

Hollow Porous Carbon-Confined Atomically Ordered PtCo 3 Intermetallics for an Efficient Oxygen Reduction Reaction

Clarifying the Origin of Ordering Effect of PtCo Intermetallic Catalysts in Catalyzing Oxygen Reduction

Synthesis of small-sized intermetallic PtCo fuel cell catalysts by promoting inner surface utilization of carbon supports

Leaching- and Sintering-Resistant Hollow or Structurally Ordered Intermetallic PtFe Alloy Catalysts for Oxygen Reduction Reactions