Thermo-Mechanical Behavior and Strain Rate Sensitivity of 3D-Printed Polylactic Acid (PLA) below Glass Transition Temperature (Tg)

Vukašin Slavković,Blaž Hanželič,Vasja Plesec,Strahinja Milenković,Gregor Harih
DOI: https://doi.org/10.3390/polym16111526
IF: 5
2024-05-29
Polymers
Abstract:This study investigated the thermomechanical behavior of 4D-printed polylactic acid (PLA), focusing on its response to varying temperatures and strain rates in a wide range below the glass transition temperature (Tg). The material was characterized using tension, compression, and dynamic mechanical thermal analysis (DMTA), confirming PLA's strong dependency on strain rate and temperature. The glass transition temperature of 4D-printed PLA was determined to be 65 °C using a thermal analysis (DMTA). The elastic modulus changed from 1045.7 MPa in the glassy phase to 1.2 MPa in the rubber phase, showing the great shape memory potential of 4D-printed PLA. The filament tension tests revealed that the material's yield stress strongly depended on the strain rate at room temperature, with values ranging from 56 MPa to 43 MPA as the strain rate decreased. Using a commercial FDM Ultimaker printer, cylindrical compression samples were 3D-printed and then characterized under thermo-mechanical conditions. Thermo-mechanical compression tests were conducted at strain rates ranging from 0.0001 s−1 to 0.1 s−1 and at temperatures below the glass transition temperature (Tg) at 25, 37, and 50 °C. The conducted experimental tests showed that the material had distinct yield stress, strain softening, and strain hardening at very large deformations. Clear strain rate dependence was observed, particularly at quasi-static rates, with the temperature and strain rate significantly influencing PLA's mechanical properties, including yield stress. Yield stress values varied from 110 MPa at room temperature with a strain rate of 0.1 s−1 to 42 MPa at 50 °C with a strain rate of 0.0001 s−1. This study also included thermo-mechanical adiabatic tests, which revealed that higher strain rates of 0.01 s−1 and 0.1 s−1 led to self-heating due to non-dissipated generated heat. This internal heating caused additional softening at higher strain rates and lower stress values. Thermal imaging revealed temperature increases of 15 °C and 18 °C for strain rates of 0.01 s−1 and 0.1 s−1, respectively.
polymer science
What problem does this paper attempt to address?
The problem that this paper attempts to solve is to study the thermomechanical behavior of 3D - printed polylactic acid (PLA) below the glass transition temperature (\(T_g\)) and its strain - rate sensitivity. Specifically, the author experimentally explored the compressive properties of 4D - printed PLA materials at different temperatures and strain rates, especially their performance under large - deformation conditions. The research focuses on: 1. **Thermomechanical properties of materials**: Evaluate the mechanical responses of PLA at different temperatures and strain rates, including the changes in parameters such as elastic modulus and yield stress. 2. **Strain - rate sensitivity**: Analyze the influence of strain rate on the mechanical properties of materials, especially the yield stress and strain hardening/softening behaviors. 3. **Self - heating phenomenon**: Explore the self - heating effect of materials at high strain rates and its influence on mechanical properties. Through these studies, the author hopes to provide basic data for the understanding and modeling of the macroscopic mechanical characteristics of 4D - printed PLA materials, and then develop a more accurate thermomechanical constitutive model for simulating material behaviors in the finite element method (FEM). In addition, the research also aims to expand the understanding of the radial and uniaxial compressive behaviors of structures with negative Poisson's ratios (such as chiral structures) at different strain rates.