Abstract:Background: Inadequate polymerization of resins is a major cause of failure in dental restorations. This study aimed to evaluate the hypothesis that both polymerization distance and preheating of four nanohybrid resins significantly affect their degree of conversion (DC). Material and methods: Four A2-colored nanohybrid resins were selected: Filtek Z250 XT (3M), Tetric N-Ceram (Ivoclar), Zafira (New Stetic), and Spectra Smart (Dentsply). These resins were chosen due to their varied compositions. Forty-eight discs (6 mm diameter, 2 mm thickness) were manufactured, with 24 discs preheated to 39°C. All discs were polymerized for 40 seconds at distances of 1 mm and 6 mm using the Bluephase N lamp (Ivoclar Vivadent), operating at 385-515 nm and 1200 mW/cm². The polymerized discs were stored in distilled water at 37°C for 24 hours, and the DC was measured using Fourier-transform infrared spectroscopy (FTIR). Statistical analysis was performed using one-way ANOVA and independent samples t-tests. Results: No statistically significant differences in DC were observed between samples preheated to 39°C and those at room temperature (p> 0.05). Zafira exhibited the highest DC, significantly higher than Z250 XT in all groups (p< 0.005) and higher than Tetric N-Ceram on the surface (p< 0.05). Significant differences were also found between Zafira and Spectra Smart in specific conditions (p< 0.05). No significant differences in DC were found between polymerization distances of 1 mm and 6 mm. Uniform polymerization was achieved throughout the resin discs. Conclusions: Preheating nanohybrid resins to 39°C had no statistically significant impact on their degree of conversion. Acceptable DC values were achieved using a high-intensity lamp for 40 seconds, even at a curing distance of 6 mm. Among the tested resins, Zafira demonstrated the highest DC under various conditions, significantly outperforming Z250 XT, Tetric N-Ceram, and Spectra Smart in specific comparisons. Key words:Nanohybrid composite, polymerization, degree of conversion.

Optimal photoinitiator concentration for light-cured dental resins

The Photoinitiators Used in Resin Based Dental Composite—A Review and Future Perspectives

Influence of photoinitiator type on the rate of polymerization, degree of conversion, hardness and yellowing of dental resin composites

Color stability, conversion, water sorption and solubility of dental composites formulated with different photoinitiator systems

Achieving property enhancements in dental resin composites via reduced concentrations of camphorquinone within a ternary initiator system

Micro-Raman spectroscopic analysis of the degree of conversion of composite resins containing different initiators cured by polywave or monowave LED units

Evaluation of the Selected Mechanical and Aesthetic Properties of Experimental Resin Dental Composites Containing 1-phenyl-1,2 Propanedione or Phenylbis(2,4,6-trimethylbenzoyl)-phosphine Oxide as a Photoinitiator

Effect of proanthocyanidins and photo-initiators on photo-polymerization of a dental adhesive

Effect of preheating and curing lamp distance on the degree of conversion of four nanohybrid resins: An in vitro study

Degree of conversion and interfacial adaptation of touch-cure resin cement polymerized by self-curing or dual-curing with reduced light

Use of NIR light and upconversion phosphors in light-curable polymers

Novel lignin α-O-4 derived hydrogen donors in CQ-based photoinitiating systems for dental resins

Effect of Optical Properties of Lithium Disilicate Glass Ceramics and Light-Curing Protocols on the Curing Performance of Resin Cement

Sunlight stability enhancement of camphorquinone based photo-curing materials via [2 + 2] cycloaddition of pyrrole ketene

Photoinitiator type and applicability of exposure reciprocity law in filled and unfilled photoactive resins

Low‐Migration Compounds with Amine Functionality as Co‐Initiators of Radical Polymerization

Multi-peak Light-emitting Diode Curing Units and Polymerization of 3D-printed Crown and Bridge Resin

The Effect of the Initiator/Activator/Accelerator Ratio on the Degree of Conversion, Film Thickness, Flow, and Cytotoxicity of Dual-Cured Self-Adhesive Resin Cements

Effects of Post-Curing Light Intensity on the Mechanical Properties and Three-Dimensional Printing Accuracy of Interim Dental Material

Initial curing characteristics of composite cements under ceramic restorations

Design of Dyes Based on the Quinoline or Quinoxaline Skeleton towards Visible Light Photoinitiators