Construction of a binary architecture of flower-like nickel phyllosilicate@zinc sulfide towards the robust, wear-resistant and thermal-stable epoxy nanocomposites

Ji-nian Yang,Zhen-yu Li,Xue-song Feng,Shi-bin Nie

DOI: https://doi.org/10.1016/j.polymdegradstab.2022.110224

IF: 5.204

2022-12-10

Polymer Degradation and Stability

Abstract:In the present study, a binary architecture of flower-like nickel phyllosilicate decorated using zinc sulfide nanoparticles () was constructed and introduced into epoxy resin (EP), yielding the robust, wear-resistant and thermal-stable nanocomposites. Several characterizations have been performed to confirm the synthesis of target and explore its positive influence on the mechanical, tribological and thermal properties of EP nanocomposites. Based on the results, could be dispersed homogeneously in the matrix without visible occurrences of debonding between interfaces, moderately improving the tensile strength and elastic modulus by 11.4% and 24.6%, respectively. The optimized tribological properties were achieved by adding 5% and the wear rate could be reduced significantly down to 0.49 × 10 −5 mm 3 /Nm, which was ca. 93% lower than pure EP. Thermal degradation analysis implied that presented improved the thermal stability, showing pronounced suppressed mass loss and elevated char residues, while kinetic analysis demonstrated the rarely changed reaction order and steadily decreased activation energy of EP along with the increased This investigation provided a facile way to prepare the robust, wear-resistant and thermal-stable EP-based tribo-materials.

polymer science