Abstract:Proceedings of the Institution of Mechanical Engineers, Part J: Journal of Engineering Tribology, Ahead of Print. Wear is a significant cause of material loss, contributing to surface degradation of crucial components, notably within engineering sectors. This article is dedicated to enhancing tribological properties through the implementation of Al2O3-based ceramic coatings, specifically targeting situations where reciprocating sliding wear predominates. This study introduces lanthanum oxide (La2O3), a rare earth oxide, as a reinforcing material in Al2O3 coatings in varying weight percentages of 1.2%, 1.6%, and 1.8% respectively along with 3% hexagonal boron nitride (h-BN). The coatings were developed by the high-velocity oxy-fuel (HVOF) surface modification technique, with SS304 serving as the substrate. The porosity, hardness, and chemical composition of the developed coatings were examined. Additionally, reciprocating tribological testing of the coatings was conducted at two loads (5 N and 15 N) under dry sliding conditions. Results indicated that coating containing 95.4% Al2O3–3% h-BN–1.6% La2O3 reduced the porosity up to 50% and improved hardness by 46% compared to the 97% Al2O3–3% h-BN coating. The formation of the α-Al2O3 phase leads to an increase in coating hardness and a reduction in porosity. Notably, the coating comprising 97% Al2O3–3% h-BN exhibited the lowest coefficient of friction among all developed coatings under both loads. Furthermore, an increase in load led to a decrease in the coefficient of friction for all developed coatings. Furthermore, the addition of La2O3 (1.6 wt%) to the coating with 3 wt% h-BN exhibited the lowest wear at both loads. The findings also revealed increased wear at high loads for all developed coatings. SEM, EDS, and XRD analysis of the worn surfaces revealed the contribution of h-BN and La2O3 in enhancing friction behavior through the formation of oxides such as α-Al2O3, B2O3, Al8B2O15, and Al11La0.497O17, along with alterations in wear mechanism and the size of wear debris. The composite coatings developed in this study shall be helpful in advanced engineering applications.

Enhancing Tribological Performance of Micro-Arc Oxidation Coatings on 6061 Aluminum Alloy with h-BN Incorporation

Effect of h-BN nanoparticles incorporation on the anti-corrosion and anti-wear properties of micro-arc oxidation coatings on 2024 aluminum alloy

Corrosion and Wear Properties of h-BN Modified TC4 Titanium Alloy Micro-Arc Oxide Coatings

Effects of nanoceramic particle size and content on the wear resistance of micro-arc oxidation coatings for 2A12 aluminum alloy

Effect of Several Inorganic Additives on Microstructure and Properties of Microarc Oxidation Coating on Aluminium Alloy

Improvement of tribological performance by micro-arc oxidation treatment on selective laser melting Ti6Al4V alloy

Micro-arc oxidation of Al alloys: mechanism, microstructure, surface properties, and fatigue damage behavior

The Effects of Na2WO4 Concentration on the Properties of Microarc Oxidation Coatings on Aluminum Alloy

Improving the Wear Resistance Properties of 7A04 Aluminum Alloy with Three Surface Modification Coatings

Microstructure and corrosion behavior of micro-arc oxidation coating on 6061 aluminum alloy pre-treated by high-temperature oxidation

Synergism of h-BN and La2O3 in improving the tribological performance of Al2O3 coatings

Improved wear and corrosion resistance of alumina alloy by MAO and PECVD

Friction Reduction of Aluminum Alloy Micro-arc Oxidation Coating by Filling Graphene Oxide

Modification of Cold-Sprayed Aluminum Coating on Nickel-Aluminum Bronze by Micro-Arc Oxidation

Improved Wear and Corrosion Resistance of Microarc Oxidation Coatings on Ti–6Al–4V Alloy with Ultrasonic Assistance for Potential Biomedical Applications

Tribological properties of aluminum alloy coated with graphene oxide/polyvinyl alcohol composites after micro-arc oxidation

Enhancing microstructural, tribological and corrosion responses of Al–Zn–Mg–Cu alloy via nano-/micro-Al2O3 particulates

Enhancing Mechanical and Tribological Properties of Cold-Sprayed Aluminum Through Graphene Nanoplatelet and Boron Carbide Reinforcement

Tribological Behavior of Microarc Oxidation Coatings Formed on Titanium Alloys Against Steel in Dry and Solid Lubrication Sliding

Processing and Analysis of Micro-Arc Oxidation Coating on 319S Aluminum Alloy

High concentration of organic solvents in aluminum MAO: A study of structural and tribological property