Abstract:This study focuses on understanding the corrosion and tribological behaviour of hybrid aluminium composites in diverse environmental conditions (dry, aqueous and alkaline). The characteristics are compared under corrosive conditions to check the tendency to wear and corrosion for its probable use in marine applications. Eutectic aluminium–silicon (Al–Si) alloys and hybrid aluminium composites enhanced with alumina (6 wt%) and varying weights of graphene nanoplatelets (GNP) (1, 2, 3 wt%) samples were fabricated by spark plasma sintering. The corrosion behaviour of the hybrid composites was investigated by potentiodynamic polarization technique using 3.5 wt% NaCl solution as electrolyte. A chromium-plated chrome steel ball of 10-mm diameter was used for the ball-on-disk test at varying load (50–250 N), sliding velocity 0.12 m/s, sliding distance 120 m, frequency 30 Hz, stroke 2 mm, and test duration 1000 s to evaluate the tribological behaviour. An increase in the corrosion and tribological performance was observed with an increase in GNP concentration in the fabricated hybrid composite sample. Composite sample with 3 wt% of GNP had the highest average electrochemical open-circuit potential value of − 0.731 V, followed by 2 wt% (− 0.743 V), 1 wt% (− 0.747 V) and base (− 0.771 V). The presence of GNP reduced the vulnerability to corrosive degradation as being superhydrophobic, it inhibited the chloride ion attack by offering lesser adsorption of the salt solution on the hybrid composites’ surfaces. The wear mechanism was discussed by interpretation from scanning electron microscopy, energy dispersive X-ray analysis (EDX) and 3D surface profilometry. The formation of carbon protective layer at the interface led to a reduction in coefficient of friction and wear of hybrid composite with 3 wt% of GNP by more than 90% and 60%, respectively, at all environmental conditions as compared to base alloy.

Tribological properties of aluminum alloy coated with graphene oxide/polyvinyl alcohol composites after micro-arc oxidation

Friction Reduction of Aluminum Alloy Micro-arc Oxidation Coating by Filling Graphene Oxide

Superhydrophobic graphene/hydrophobic polymer coating on a microarc oxidized metal surface

Tribological Properties of Carbonized Polydopamine/rgo Composite Coatings

Hybrid epoxy-SiO2/GO nanosheets anti-corrosive coating for aeronautic aluminum Al6061-T5

Enhancing Tribological Performance of Micro-Arc Oxidation Coatings on 6061 Aluminum Alloy with h-BN Incorporation

Friction and Wear Behavior of Graphene-Modified Titanium Alloy Micro-arc Oxidation Coatings

Tribological properties of graphene oxide reinforced aramid paper-based composites

Investigation of Mechanical and Tribological Properties of Al7075-Al2O3-GNPs Hybrid Composites Produced by Powder Metallurgy and Induction Hot Pressing

A "bricks-and-mortar" structured graphene oxide/polyvinyl alcohol coating: enhanced water interfacial lubrication and durability

Tribological properties of alkylated reduced graphene oxide as lubricant additive

High concentration of organic solvents in aluminum MAO: A study of structural and tribological property

Graphene oxide/Al composites with enhanced mechanical properties fabricated by simple electrostatic interaction and powder metallurgy

Construction of lubricant composite coating on Ti6Al4V alloy using micro-arc oxidation and grafting hydrophilic polymer

Tribological properties of Al-GNP composites at elevated temperature

Study of the Protection of Aluminum Alloy Surfaces by a Graphene-Modified Fluorocarbon Anticorrosive Coating

Friction and wear behavior of micro‐arc oxidation‐modified graphene/epoxy resin composite coating on TC4 titanium alloyReibungs‐ und Verschleißverhalten einer durch Mikro‐Lichtbogen‐Oxidation modifizierten Graphen/Epoxidharz‐Verbundbeschichtung auf einer TC4‐Titanlegierung

Preparation and lubrication properties of graphene oxide/polyethylene glycol/polyvinyl alcohol composite film

Corrosion and Tribo-Investigations on Alumina–Graphene-Doped Hybrid Aluminium Composites

Preparation and tribological behaviors of poly (ether ether ketone) nanocomposite films containing graphene oxide nanosheets

Graphene oxide-reinforced aluminum alloy matrix composite materials fabricated by powder metallurgy