Abstract:Statement of problem: Previous studies have shown casting methodology to influence the as-cast properties of dental casting alloys. It is important to consider clinically important mechanical properties so that the influence of casting can be clarified. Purpose: The purpose of this study was to evaluate how torch/centrifugal and inductively cast and vacuum-pressure casting machines may affect the castability, microhardness, chemical composition, and microstructure of 2 high noble, 1 noble, and 1 base metal dental casting alloys. Material and methods: Two commonly used methods for casting were selected for comparison: torch/centrifugal casting and inductively heated/ vacuum-pressure casting. One hundred and twenty castability patterns were fabricated and divided into 8 groups. Four groups were torch/centrifugally cast in Olympia (O), Jelenko O (JO), Genesis II (G), and Liberty (L) alloys. Similarly, 4 groups were cast in O, JO, G, and L by an inductively induction/vacuum-pressure casting machine. Each specimen was evaluated for casting completeness to determine a castability value, while porosity was determined by standard x-ray techniques. Each group was metallographically prepared for further evaluation that included chemical composition, Vickers microhardness, and grain analysis of microstructure. Two-way ANOVA was used to determine significant differences among the main effects. Statistically significant effects were examined further with the Tukey HSD procedure for multiple comparisons. Data obtained from the castability experiments were non-normal and the variances were unequal. They were analyzed statistically with the Kruskal-Wallis rank sum test. Significant results were further investigated statistically with the Steel-Dwass method for multiple comparisons (α=.05). Results: The alloy type had a significant effect on surface microhardness (P<.001). In contrast, the technique used for casting did not affect the microhardness of the test specimen (P=.465). Similarly, the interaction between the alloy and casting technique was not significant (P=.119). A high level of castability (98.5% on average) was achieved overall. The frequency of casting failures as a function of alloy type and casting method was determined. Failure was defined as a castability index score of <100%. Three of 28 possible comparisons between alloy and casting combinations were statistically significant. The results suggested that casting technique affects the castability index of alloys. Radiographic analysis detected large porosities in regions near the edge of the castability pattern and infrequently adjacent to noncast segments. All castings acquired traces of elements found in the casting crucibles. The grain size for each dental casting alloy was generally finer for specimens produced by the induction/vacuum-pressure method. The difference was substantial for JO and L. Conclusions: This study demonstrated a relation between casting techniques and some physical properties of metal ceramic casting alloys.

The effect of sprue attachment design on castability and porosity

Investigation of the effect of three sprue designs on the porosity and the completeness of titanium cast removable partial denture frameworks

Effect of Machining Method and Margin Design on the Accuracy and Margin Quality of Monolithic Zirconia Crowns

Casting made simple using modified sprue design: an in vitro study

Effect of production method on surface roughness, marginal and internal fit, and retention of cobalt-chromium single crowns

Analysis of four dental alloys following torch/centrifugal and induction/ vacuum-pressure casting procedures

Bond strengths of porcelain to cobalt-chromium alloys made by casting, milling, and selective laser melting

Effect of porcelain firing and cementation on the marginal fit of implant-supported metal-ceramic restorations fabricated by additive or subtractive manufacturing methods

Effect of feed sprue size on porosity defects in Platinum 950 centrifugal investment casting via numerical modelling

Effects of Repeated Firing on the Marginal Accuracy of Co-Cr Copings Fabricated by Selective Laser Melting

Comparison between selective laser melted and cast removable partial denture frameworks

Effect of Luting Materials on the Accuracy of Fit of Zirconia Copings: A Non-Destructive Digital Analysis Method

Marginal discrepancy of 3-unit Co-Cr metal copings fabricated with additive and subtractive manners: A comparative study

Effect of freezing range on reducing casting defects through 3D sand-printed mold designs

Studies on the castability of Co-Cr alloy for cast plates. Part 1: The effects of sprue attachment direction to wax plates and the investment direction of refractory models

The effects of abutment wall height, platform size, and screw access channel filling method on resistance to dislodgement of cement-retained, implant-supported restorations

Influence of recasting palladium-silver alloy on the fit of crowns with different marginal configurations

Discrepancy at the implant abutment-prosthesis interface of complete-arch cobalt-chromium implant frameworks fabricated by additive and subtractive technologies before and after ceramic veneering

Marginal accuracy of nickel chromium copings fabricated by conventional and accelerated casting procedures, produced with ringless and metal ring investment procedures: A comparative in vitro study

Adhesion of veneering porcelain to cobalt-chromium dental alloys processed with casting, milling, and additive manufacturing methods: A systematic review and meta-analysis

The effect of veneer on the marginal fit of the copings using different materials