Abstract:Highlights • scCO 2 foaming and melt-extrusion were used to produce reinforced scaffolds. • Creation of foams with high-porosity, homogeneity and reinforcement. • Pressure had a significant influence on pore size and compressive strength. • Stresses similar to trabecular bone were obtained for Mg(OH) 2 and HAp foams. Background As an alternative to conventional medicine, scaffolds have emerged to mimic and/or replace damaged tissue. 3D porous matrix scaffolds made of biodegradable and biocompatible polymers, including PLGA, have proven to be of particular interest for use as bone substitutes in Tissue Engineering. Methods The study used high-pressure CO 2 foaming to produce PLGA-based foams. Previously, melt-extrusion was used to introduce reinforcement agents, Mg(OH) 2 , Hydroxyapatite (HAp) and Mg, to achieve foams with improved properties. Foam morphology was analysed using SEM, EDS, and 3D scanner techniques, and foam strength was measured using compression tests. A statistical analysis was carried out to study the effect of pressure and temperature on foams pore size and hardness. Significant findings The foams produced were rigid, non-sticky and time-stable, and showed high porosity. The pressure was found to be the only significant variable to tune both porosity and cell densities of scaffolds. Setting a pore size at 500 μm, compressive stresses of 1.85 MPa, 3.81 MPa were achieved for Mg(OH) 2 and HAp, respectively. Those results were comparable to literature ́s trabecular bovine bone compression resistance of 4.2 MPa. This finding indicated the possibility of getting, at the same time, convenient results for porosity and mechanical resistance for their use as bone replacement agents. Finally, a 20 % w/w ratio of reinforcing agent was found to produce the best pore size-stress ratio. Graphical abstract Download : Download high-res image (182KB) Download : Download full-size image

Preparation of magnetic scaffolds via supercritical carbon dioxide foaming process using iron oxide nanoparticles coated with CO2‐philic materials as nucleating agents

Effect of Foreign Ion Substitution and Micropore Tuning in Robocasting Single-Phase Bioceramic Scaffolds on the Physicochemical Property and Vascularization

Control of pore size and structure of tissue engineering scaffolds produced by supercritical fluid processing.

Enhancing polymeric bone scaffolds mechanical characteristics using supercritical CO 2 foaming and reinforcing agents

Ferroferric Oxide/chitosan Scaffolds with Three-Dimensional Oriented Structure

Modulatory Effects of the Composition and Structure on the Osteogenic Enhancement for Superparamagnetic Scaffolds

Development of Scaffolds with Chitosan Magnetically Activated with Cobalt Nanoferrite: A Study on Physical-Chemical, Mechanical, Cytotoxic and Antimicrobial Behavior

Foaming of PCL-Based Composites Using scCO2: Structure and Physical Properties

Synergistic Effect of Static Magnetic Fields and 3D-Printed Iron-Oxide-Nanoparticle-Containing Calcium Silicate/Poly-ε-Caprolactone Scaffolds for Bone Tissue Engineering

Magnetic Cell–Scaffold Interface Constructed by Superparamagnetic IONP Enhanced Osteogenesis of Adipose-Derived Stem Cells

Preparation and characterization of 3D porous conductive scaffolds with magnetic resonance enhancement in tissue engineering

Design and synthesis of novel polycaprolactone-chitosan based scaffolds using supercritical carbon dioxide

Fabrication of porous scaffolds using NaHCO3 particulates as the porogen material

Incorporation of Superparamagnetic Iron Oxide Nanoparticles into Collagen Formulation for 3D Electrospun Scaffolds

Foaming of PCL-Based Composites Using scCO2—Biocompatibility and Evaluation for Biomedical Applications

Supercritical carbon dioxide assisted fabrication of biomimetic sodium alginate/silk fibroin nanofibrous scaffolds

Electrospun Fibrous Scaffolds with Iron-Doped Hydroxyapatite Exhibit Osteogenic Potential with Static Magnetic Field Exposure

Smart Biopolymer Scaffolds Based on Hyaluronic Acid and Carbonyl Iron Microparticles: 3D Printing, Magneto-Responsive, and Cytotoxicity Study

Fabrication of 3D-Printed Biodegradable Porous Scaffolds Combining Multi-Material Fused Deposition Modeling and Supercritical CO2 Techniques

Magnetical scafford with ROS-scavenging for bone regeneration under static magnetic field

Novel Magnetic Cell-Scaffold Construct with and Without Magnetic Field Enhanced Osteogenesis of Stem Cells and Formation of New Bone