Abstract:A series of perovskite-type La1-xSrxCo1-yFeyO3 catalysts were successfully prepared by the citric acid-EDTA complexation. The catalysts exhibited excellent catalytic oxidation soot activity and sulfur resistance. The characterization of X-ray diffraction (XRD), fourier transform infrared spectra (FT-IR), scanning electron microscope (SEM), H-2-temperature-programmed reduction (H-2-TPR), X-ray photoelectron spectroscopy (XPS) and SO2-temperature programmed desorption (SO2-TPD) were used to reveal the effect of Sr and Fe doping on the physicochemical properties and sulfur tolerance of La1-xSrxCo1-yFeyO3 catalysts. Experimental results demonstrated that when the Sr doped with LaCoO3, it was beneficial for the catalyst to form more surface adsorption oxygen (O-2(-) or O-) and oxygen vacancies, thereby improving both the low-temperature redox ability and catalytic oxidation soot activity of catalyst. T-i (ignition temperature of soot) and T-m (complete conversion temperature of soot) are only 284 and 347 degrees C. Furthermore, with the doping of Fe, the low-temperature redox performance of catalyst was further improved, because the high-valent ions (Fe4+) were formed in the surface of catalyst, the Fe4+ ion could enhance the oxidation soot activity of catalyst. Moreover, the poisoning of SO2 was mainly attributed to the sulfation (SO32-, SO42-) of Co2+/Co3+ and surface adsorbed oxygen, leading to deactivating the active site (O-2(-) or O- and Fe4+) of catalyst. Simultaneous doping of Sr and Fe can form a strong interaction, which can effectively inhibit the deposition of sulfur species on the catalyst surface and reduce the poisoning of SO2 into the catalyst. Both XPS and SO2-TPD characterizations showed that the sulfur resistance of catalyst was mainly attributed the competitive adsorption of metal ions (Fe3+) on SO2, which could effectively reduce the poisoning of SO2 on the surface adsorption oxygen and Fe'. TPO (temperature programmed oxidation) activity characterization showed that LaSrCoFeO3-S still maintained good catalytic oxidation soot activity. T-i and T-m, were 320 and 361 degrees C, respectively, indicating that the simultaneous doping of Sr and Fe has excellent low-temperature catalytic soot activity and good sulfur poisoning ability.

Formation and soot combustion of honeycomb-like LaFeO3 microfibers

Soot Trapping and Combustion on Nanofibrous Perovskite LaMnO3 Catalysts under a Continuous Flow of Soot

Soot Combustion Performance and H2-TPR Study on Ceria-Based Mixed Oxides

Preparation of aluminum borate whiskers/CoxCr3‐xO4 catalysts on channel surface of cordierite honeycomb ceramic for soot catalytic combustion

Preparation of Metallic Monolithic Pt/FeCrAl Fiber Catalyst by Suspension Spraying for VOCs Combustion.

Preparation, Characterization and Optical Property of LaFeO3 Nanoparticles via Sol-Gel Combustion Method

Preparation and characterization of Na4Mn9O18 whiskers on channel surface of cordierite honeycomb ceramics for soot catalytic combustion

Preparation, Structure and Soot Oxidation Performance of Nano-scaled Perovskite-type La1-xKxCoO3 Catalyst

Potassium promoted Fe–Ce composite oxides monolithic catalysts for catalytic soot combustion

Hydrothermal Conversion of Fe2o3/Sio2 Spheres into Fe2o3/Silicalite-1 Nanowires: Synthesis, Characterization, and Catalytic Properties

Surface tuning of 3DOM LaFe0.6Mg0.4O3 perovskite by acid etching to enhance catalytic performance for soot combustion

Photocataltic reduction of CO2 by nanometer LaFeO3-TiO2

ene on the nanostructure and functional groups of soot in a propane / oxygen di ff usion fl ame

Preparation and performance of a nano-honeycomb cathode for microtubular solid oxide fuel cells

Facilitating Catalytic Purification of Auto-Exhaust Carbon Particles via the Fe 2 O 3 {113} Facet-dependent Effect in Pt/Fe 2 O 3 Catalysts

Preparation of CoFe 2 O 4 -Doped TiO 2 Nanofibers by Electrospinning and Annealing for Oxygen Electrocatalysis

Effect of Sr and Fe Doped LaCoO3 on Catalytic Oxidation of Soot and Sulfur Resistance

Alkali metal and alkali earth metal-modified La-Fe-based perovskite catalyzed coke combustion

Effect of Calcination Temperature on Structural Properties and Catalytic Soot Combustion Activity of MnOx/wire-mesh Monoliths

Nanoscale structural transformations in LaFeO 3 oxygen carriers for enhanced reactivity in chemical looping combustion

Integrating Pd-doped perovskite catalysts with ceramic hollow fibre substrate for efficient CO oxidation