Abstract:Ti-6Al-4V selective dissolution occurs in vivo on orthopedic implants as the leading edge of a pitting corrosion attack. A gap persists in our fundamental understanding of selective dissolution and pre-clinical tests fail to reproduce this damage. While CoCrMo clinical use decreases, Ti-6Al-4V and the crevice geometries where corrosion can occur remain ubiquitous in implant design. Additionally, most additively manufactured devices cleared by the FDA use Ti-6Al-4V. Accelerated preclinical testing, therefore, would aid in the evaluation of new titanium devices and biomaterials. In this study, using temperature, we (1) developed an accelerated pre-clinical methodology to rapidly induce dissolution and (2) investigated the structure-property relationship between the dissolving surface and the oxide layer. We hypothesized that solution temperature and H2O2 concentration would accelerate oxide degradation, increase corrosion kinetics and decrease experimental times. To assess this effect, we selected temperatures above (45 °C), below (24 °C), and at (37 °C) physiological levels. Then, we acquired electrochemical impedance spectra during active β dissolution, showing significant decreases in oxide polarization resistance (Rp) both over time (p = 0.000) and as temperature increased (p = 0.000). Next, using the impedance response as a guide, we quantified the extent of selective dissolution in scanning electron micrographs. As the temperature increased, the corrosion rate increased in an Arrhenius-dependent manner. Last, we identified three surface classes as the oxide properties changed: undissolved, transition and dissolved. These results indicate a concentration and temperature dependent structure-property relationship between the solution, the protective oxide film, and the substrate alloy. Additionally, we show how supraphysiological temperatures induce structurally similar dissolution to tests run at 37 °C in less experimental time. STATEMENT OF SIGNIFICANCE: Within modular taper junctions of total hip replacement systems, retrieval studies document severe corrosion including Ti-6AL-4V selective dissolution. Current pre-clinical tests and ASTM standards fail to reproduce this damage, preventing accurate screening of titanium-based biomaterials and implant designs. In this study, we induce selective dissolution using accelerated temperatures. Building off previous work, we use electrochemical impedance spectroscopy to rapidly monitor the oxide film during dissolution. We elucidate components of the dissolution mechanism, where oxide degradation precedes pit nucleation within the β phase. Using an Arrhenius approach, we relate these accelerated testing conditions to more physiologically relevant solution concentrations. In total, this study shows the importance of including adverse electrochemical events like cathodic activation and inflammatory species in pre-clinical testing.

The influence of cathodic polarization and simulated inflammation on titanium electrochemistry

Preclinical EIS Study of the Inflammatory Response Evolution of Pure Titanium Implant in Hank's Biological Solution

Effects of open circuit immersion and vertex potential on potentiodynamic polarization scans of metallic biomaterials

CORROSION RESISTANCE OF β-PHASE TITANIUM ALLOYS UNDER SIMULATED INFLAMMATORY CONDITIONS: EXPLORING THE RELEVANCE OF BIOCOMPATIBLE ALLOYING ELEMENTS

The reduction half cell in biomaterials corrosion: oxygen diffusion profiles near and cell response to polarized titanium surfaces

Electrochemical Corrosion of Titanium and Titanium Alloys Anodized in H2SO4 and H3PO4 Solutions

Impact of simulated inflammation and food breakdown on the synergistic interaction between corrosion and wear on titanium

The electrochemical behavior of a Ti50Ni47Fe3 shape memory alloy

Determinants of corrosion resistance of Ti-6Al-4V alloy dental implants in an In Vitro model of peri-implant inflammation

Electrochemical Corrosion Behavior of Biomedical Ti–22Nb and Ti–22Nb–6Zr Alloys in Saline Medium

Influence of Cupric, Ferric, and Chloride on the Corrosion of Titanium in Sulfuric Acid Solutions Up to 85°C

The effect of simulated inflammatory conditions on the corrosion of Mg, Fe and CoCrMo

Oxide degradation precedes additively manufactured Ti-6Al-4V selective dissolution: An unsupervised machine learning correlation of impedance and dissolution compared to Ti-29Nb-21Zr

Increasing temperature accelerates Ti-6Al-4V oxide degradation and selective dissolution: An Arrhenius-based analysis

Evaluation of Corrosion Behavior by Measuring Passivation Current Density of Dental Implant Coated with Bioceramic Materials

Improving Pure Titanium's Biological and Mechanical Characteristics through ECAP and Micro-Arc Oxidation Processes

Corrosion and conductivity behavior of titanium-doped amorphous carbon film coated SS316L in the environment of PEMFCs

Corrosion behavior and electrochemical properties of carbon steel, commercial pure titanium, copper and copper–aluminum–nickel alloy in 3.5% sodium chloride containing sulfide ions

Reactive Oxygen Species, Electrode Potential and pH Affect CoCrMo Alloy Corrosion and Semiconducting Behavior in Simulated Inflammatory Environments

The effect of etched 3D printed Cu-bearing titanium alloy on the polarization of macrophage

Corrosion Investigation by Scanning Electrochemical Microscopy of AISI 446 and Ti-Coated AISI 446 Ferritic Stainless Steel as Potential Material for Bipolar Plate in PEMWE