Deposition Strategy on Microstructure Development and Mechanical Properties of Wire Arc Additively Manufactured Austenitic Stainless Steel

Gaurav Kishor,Krishna Kishore Mugada,Raju Prasad Mahto,Vishvesh Badheka

DOI: https://doi.org/10.1007/s11665-024-10511-9

IF: 2.3

2024-12-05

Journal of Materials Engineering and Performance

Abstract:Deposition of a thin wall using a unidirectional deposition strategy in the wire arc additive manufacturing process leads to heat accumulation and subsequent softening of layers resulting in the non-uniform thickness of layers and dimensional inaccuracies which leads to defects in the as-deposited samples. Therefore, an alternative bidirectional deposition that balances the heat accumulation is utilized to deposit the samples. A detailed investigation is carried out to understand the effect of deposition strategy on microstructure formation, tensile properties, and, hardness. The results indicate the formation of γ-austenite, δ-ferrite, and equiaxed grains in the bottom region. In the middle region, coarser grains and a columnar dendritic structure were observed. The top region exhibited finer grains compared to the middle region, along with dendrites featuring secondary arms. The grain size varies from the fusion region (8.82 μm) to the top region (19.06 μm) along the building direction. The bottom and top regions displayed higher dislocation density, microstrain, and a smaller crystallite size than the middle region. Later, tensile strength and hardness were studied, and found that the bidirectional strategy showed a higher average yield strength (380 MPa), and the unidirectional strategy (330 MPa) and ultimate tensile strength varied from a unidirectional strategy (600 MPa) to a bidirectional strategy (675 MPa). As-deposited samples show greater hardness in top layers such as unidirectional (around 180 HV) and bi-directional (around 184 HV).

materials science, multidisciplinary