Abstract:A straightforward, continuous, and scalable method to synthesize s‐SWCNTs is developed. High‐purity and individual s‐SWCNTs of small‐diameters distribution (≈1 nm) are produced by gas‐phase synthesis, showing promising electrical properties and potential for electronic device applications. The large‐scale synthesis of high‐purity semiconducting single‐walled carbon nanotubes (s‐SWCNTs) plays a crucial role in fabricating high‐performance and multiapplication‐scenario electronics. This work develops a straightforward, continuous, and scalable method to synthesize high‐purity and individual s‐SWCNTs with small‐diameters distribution (≈1 nm). It is believed that the water and carbon dioxide resulting from the decomposition of isopropanol act as oxidizing agents and selectively etch metallic SWCNTs, hence enhancing the production of s‐SWCNTs. The performance of individual‐SWCNTs field effect transistors confirms the high abundance of s‐SWCNTs, presenting a mean mobility of 376 cm2 V−1 s−1 and a high mobility of 2725 cm2 V−1 s−1 with an on‐current to off‐current (Ion/Ioff) ratio as high as 2.51 × 107. Moreover, thin‐film transistors based on the as‐synthesized SWCNTs exhibit excellent performance with a mean mobility of 9.3 cm2 V−1 s−1 and Ion/Ioff ratio of 1.3× 105, respectively, verifying the enrichment of s‐SWCNTs. This work presents a simple and feasible route for the sustainable synthesis of high‐quality s‐SWCNTs for electronic devices.

Bulk synthesis of large diameter semiconducting single-walled carbon nanotubes by oxygen-assisted floating catalyst chemical vapor deposition.

Water-Assisted Preparation of High-Purity Semiconducting (14,4) Carbon Nanotubes

Preparation of isolated semiconducting single-wall carbon nanotubes by oxygen-assisted floating catalyst chemical vapor deposition

Large‐Scale Synthesis of Rings of Bundled Single‐Walled Carbon Nanotubes by Floating Chemical Vapor Deposition

Selective growth of semiconducting single-walled carbon nanotubes solely from carbon monoxide

Scalable growth of single-walled carbon nanotubes with a highly uniform structure

Synthesis Of Large Quantity Single-Walled Carbon Nanotubes By Arc Discharge

Efficient Fabrication of High-Quality Single-Walled Carbon Nanotubes and Their Macroscopic Conductive Fibers

Direct Synthesis of Semiconducting Single‐Walled Carbon Nanotubes Toward High‐Performance Electronics

Towards the synthesis of semiconducting single-walled carbon nanotubes by floating-catalyst chemical vapor deposition: Challenges of reproducibility

Spatially Confined CVD Growth of High‐Density Semiconducting Single‐Walled Carbon Nanotube Horizontal Arrays

Growth of close-packed semiconducting single-walled carbon nanotube arrays using oxygen-deficient TiO2 nanoparticles as catalysts

Synthesis of Single-Walled Carbon Nanotubes by the Vertical Floating Catalyst Method

Large Scale Synthesis of Single-Wall Carbon Nanotubes by Arc-Discharge Method

Enrichment of Large-Diameter Semiconducting Single-Walled Carbon Nanotubes by Conjugated Polymer-Assisted Separation

Single-Walled Carbon Nanotube Thin Film with High Semiconducting Purity by Aerosol Etching toward Thin-Film Transistors

Nearly Exclusive Growth of Small Diameter Semiconducting Single-Wall Carbon Nanotubes from Organic Chemistry Synthetic End-Cap Molecules

Diameter-Specific Growth Of Semiconducting Swnt Arrays Using Uniform Mo2c Solid Catalyst

Diameter controlled growth of single-walled carbon nanotubes from SiO2 nanoparticles

Towards the preparation of single-walled carbon nanotubes with average diameter of 1.2 nm

Growth of Single-Walled Carbon Nanotubes with Controlled Structure: Floating Carbide Solid Catalysts