Abstract:Motivated by recent advancements highlighting Ta as a promising material in low-loss superconducting circuits and showing long coherence times in superconducting qubits, we have explored the effect of cryogenic temperatures on the growth of Ta and its integration in superconducting circuits. Cryogenic growth of Ta using a low temperature molecular beam epitaxy (MBE) system is found to stabilize single phase $\alpha$-Ta on several different substrates, which include Al$\mathrm{_2}$O$\mathrm{_3}$(0001), Si(001), Si(111), SiN${_x}$, and GaAs(001). The substrates are actively cooled down to cryogenic temperatures and remain < 20 K during the Ta deposition. X-ray $\theta$-2$\theta$ diffraction after warming to room temperature indicates the formation of polycrystalline $\alpha$-Ta. The 50 nm $\alpha$-Ta films grown on Al$\mathrm{_2}$O$\mathrm{_3}$(0001) at a substrate manipulator temperature of 7 K have a room temperature resistivity ($\mathrm{\rho _{300 K}}$) of 13.4 $\mathrm{\mu \Omega}$cm, a residual resistivity ratio (RRR) of 17.3 and a superconducting transition temperature (T$_C$) of 4.14 K, which are comparable to bulk values. In addition, atomic force microscopy (AFM) indicates that the film grown at 7 K with an RMS roughness of 0.45 nm was significantly smoother than the one grown at room temperature. Similar properties are found for films grown on other substrates. Results for films grown at higher substrate manipulator temperatures show higher $\mathrm{\rho _{300 K}}$, lower RRR and Tc, and increased $\beta$-Ta content. Coplanar waveguide resonators with a gap width of 3 $\mathrm{\mu}$m fabricated from cryogenically grown Ta on Si(111) and Al$\mathrm{_2}$O$\mathrm{_3}$(0001) show low power Q$_i$ of 1.9 million and 0.7 million, respectively, indicating polycrystalline $\alpha$-Ta films may be promising for superconducting qubit applications even though they are not fully epitaxial.

Engineering high-Q superconducting tantalum microwave coplanar waveguide resonators for compact coherent quantum circuits

Tantalum thin films sputtered on silicon and on different seed layers: material characterization and coplanar waveguide resonator performance

Tantalum Microwave Resonators with Ultra-High Intrinsic Quality Factors

Microwave characterization of tantalum superconducting resonators on silicon substrate with niobium buffer layer

Low-loss α-tantalum coplanar waveguide resonators on silicon wafers: fabrication, characterization and surface modification

Stable and low loss oxide layer on α-Ta (110) film for superconducting qubits

Low-loss low thermo-optic coefficient Ta 2 O 5 on crystal quartz planar optical waveguides

Minimizing Kinetic Inductance in Tantalum-Based Superconducting Coplanar Waveguide Resonators for Alleviating Frequency Fluctuation Issues

Cryogenic growth of tantalum thin films for low-loss superconducting circuits

Tantalum airbridges for scalable superconducting quantum processors

High-Q trenched aluminum coplanar resonators with an ultrasonic edge microcutting for superconducting quantum devices

Chemical Mechanical Planarization for Ta-based Superconducting Quantum Devices

Growth and Structure of alpha-Ta films for Quantum Circuit Integration

Two-Level Systems in Nucleated and Non-Nucleated Epitaxial alpha-Tantalum films

Characterizing Niobium Nitride Superconducting Microwave Coplanar Waveguide Resonator Array for Circuit Quantum Electrodynamics in Extreme Conditions

Ultrathin Magnesium-based Coating as an Efficient Oxygen Barrier for Superconducting Circuit Materials

Fabrication of Ultra-High-q Ta2O5 Microdisks by Photolithography-Assisted Chemo-Mechanical Etching

Structure and Formation Mechanisms in Tantalum and Niobium Oxides in Superconducting Quantum Circuits

Niobium coaxial cavities with internal quality factors exceeding 1.5 billion for circuit quantum electrodynamics

Substrate surface engineering for high-quality silicon/aluminum superconducting resonators