Abstract:Following long-standing predictions associated with hydrogen, high-temperature superconductivity has recently been observed in several hydride-based materials. Nevertheless, these high-$T_c$ phases only exist at extremely high pressures, and achieving high transition temperatures at ambient pressure remains a major challenge. Recent predictions of the complex hydride Mg$_{2}$IrH$_{6}$ may help overcome this challenge with calculations of high-$T_c$ superconductivity (65 K$~<~T_c~<~$ 170 K) in a material that is stable at atmospheric pressure. In this work, the synthesis of Mg$_{2}$IrH$_{6}$ was targeted over a broad range of $P$-$T$ conditions, and the resulting products were characterized using X-ray diffraction (XRD) and vibrational spectroscopy, in concert with first-principles calculations. The results indicate that the charge-balanced complex hydride Mg$_{2}$IrH$_{5}$ is more stable over all conditions tested up to ca 28 GPa. The resulting hydride is isostructural with the predicted superconducting Mg$_{2}$IrH$_{6}$ phase except for a single hydrogen vacancy, which shows a favorable replacement barrier upon insertion of hydrogen into the lattice. Bulk Mg$_{2}$IrH$_{5}$ is readily accessible at mild $P$-$T$ conditions and may thus represent a convenient platform to access superconducting Mg$_{2}$IrH$_{6}$ via non-equilibrium processing methods.

What problem does this paper attempt to address?

The paper primarily explores the synthesis and properties of magnesium iridium hydride (Mg2IrHx), aiming to find potential pathways to achieve high-temperature superconductivity at ambient pressure. Specifically, the research team focused on the complex hydride Mg2IrH6, which has garnered attention due to its predicted ability to exhibit a relatively high superconducting transition temperature (Tc) at atmospheric pressure. However, the direct synthesis of Mg2IrH6 poses challenges in experiments, leading researchers to explore the synthesis of Mg2IrH5 instead, finding it to be more stable under a broad range of pressure-temperature (P-T) conditions. Through high-pressure diamond anvil cell (DAC) experiments and first-principles calculations, the researchers confirmed the formation of Mg2IrH5, which structurally resembles Mg2IrH6 but with disordered vacancies of hydrogen atoms, i.e., each IrH6 octahedron unit is missing one hydrogen atom, forming an [IrH5]4- complex. This vacancy leads to Mg2IrH5 being more stable than Mg2IrH6 under all tested conditions, especially at pressures up to about 28 GPa. The crystal structure of Mg2IrH5 is the same as that of Mg2IrH6, both being face-centered cubic (FCC), but due to the disordered distribution of hydrogen atoms, it is thermodynamically more stable. Although Mg2IrH5 is non-superconducting, its structural similarity to Mg2IrH6 implies that by using non-equilibrium processing methods, such as depositing or implanting additional hydrogen atoms, Mg2IrH5 could potentially be transformed into the superconducting state of Mg2IrH6. The study also utilized Raman spectroscopy and infrared spectroscopy for sample characterization, and the results indicated that the local hydrogen environment of the samples remained consistent regardless of the synthesis conditions, further supporting the formation of Mg2IrH5. Additionally, computational results suggested that there is no significant energy barrier for the transformation from Mg2IrH5 to Mg2IrH6, meaning that the transition from an insulating to a superconducting state could be achieved by controlling the addition of hydrogen. In summary, the research provides a pathway to prepare Mg2IrH6 with potential high-temperature superconductivity at lower pressure conditions, that is, by first synthesizing Mg2IrH5 and then inserting additional hydrogen atoms through non-equilibrium processing techniques, potentially overcoming the significant challenge of achieving high Tc superconductivity at conventional pressures.

Synthesis of Mg$_2$IrH$_5$: A potential pathway to high-$T_c$ hydride superconductivity at ambient pressure

Feasible route to high-temperature ambient-pressure hydride superconductivity

Enhancement for Phonon-Mediated Superconductivity Up to 37 K in Few-Hydrogen Metal-Bonded Layered Magnesium Hydride under Atmospheric Pressure

First-Principles Study of High-Temperature Superconductivity in X2MH6 Compounds under 20 GPa

Realizing high-Tc ambient-pressure superconductivity in hole-doped hydride Mg(BH4)2

Hydrogen anion unit and high-temperature superconductivity in ternary hydride Mg 3 TiH 12 under moderate pressures

High-temperature superconductivity below 100 GPa in ternary C-based hydride M C 2 H 8 with molecular crystal characteristics ( M = Na, K, Mg, Al, and Ga)

Prediction of Ambient Pressure Conventional Superconductivity above 80K in Thermodynamically Stable Hydride Compounds

Tuning Chemical Precompression: Theoretical Design and Crystal Chemistry of Novel Hydrides in the Quest for Warm and Light Superconductivity at Ambient Pressures

High-temperature Superconductivity in Sulfur Hydride Evidenced by Alternating-Current Magnetic Susceptibility

Superconductive "sodalite"-like clathrate calcium hydride at high pressures

Unlocking the Origin of High‐Temperature Superconductivity in Molecular Hydrides at Moderate Pressures

Data-driven design of high-temperature superconductivity among ternary hydrides under pressure

Prediction of ambient pressure superconductivity in cubic ternary hydrides with MH$_6$ octahedra

Prediction of ambient pressure conventional superconductivity above 80 K in hydride compounds

Fermi Surface Topology and Anisotropic Superconducting Gap in Electron-Doped Hydride Compounds at High Pressure

Prediction of ambient pressure superconductivity in cubic ternary hydrides with MH6 octahedra

Designing Quaternary Hydrides with Potential High T$_c$ Superconductivity

Low-Pressure Electrochemical Synthesis of Complex High-Pressure Superconducting Superhydrides

Metal-bonded perovskite lead hydride with phonon-mediated superconductivity exceeding 46 K under ambient pressure

Designing ternary superconducting hydrides with A15-type structure at moderate pressures