Abstract:Recently, ternary clathrate hydrides are promising candidates for high-temperature superconductor. However, it is a formidable challenge to effectively hunt high-temperature superconductivity among multinary hydrides due to the expensive computational cost associated with large unit cells and huge stoichiometric choices. Here we present an efficiently data-driven strategy, including generated clathrate frameworks, the quick estimation of stability for each framework and superconducting critical temperature (Tc) for each hydride structure, to accelerate the discovery of high-temperature superconducting hydrides. Our strategy was initialized with more than one million input structures via zeolite databases and our generated dataset. As a result, such a strategy hitherto uncovered 14 prototypical hydrogen frameworks for clathrate hydrides, which is 1.5 times greater than the number (9) of previously reported prototypes. Remarkably, eleven ternary clathrate structures were predicted to have Tcs above 250 K at 300 GPa. Further extensive global structure-searching simulations support that Li2NaH17 and ThY2H24 are thermodynamically stable at 220 and 150 GPa, respectively, with Tcs approaching room temperature of 297 K and 303 K, which are promising for future synthesis. These results offer a platform to explore high-temperature superconductors via a great number of databases.

What problem does this paper attempt to address?

The main problem that this paper attempts to solve is how to efficiently screen out ternary hydrides with high - temperature superconducting characteristics under high - pressure conditions. Specifically, the research aims to overcome the problem of high computational cost caused by complex stoichiometry and large unit cells, thereby accelerating the discovery of high - temperature superconductors. The following are the core issues of the paper: 1. **Efficient screening of high - temperature superconductors**: Traditional crystal structure prediction methods face huge challenges when dealing with multi - component hydrides because the structures of these compounds are complex and the amount of calculation is huge. Therefore, it is necessary to develop a data - driven method to quickly screen potential high - temperature superconducting materials. 2. **Explore new high - temperature superconducting frameworks**: There are few known high - temperature superconducting hydride prototypes, mainly concentrated on a few structures. By mining a large amount of structural information in the database, researchers hope to find more potential high - temperature superconducting frameworks. 3. **Improve prediction accuracy**: In order to ensure the reliability of the prediction, the research team needs not only to identify stable structures but also to accurately estimate the superconducting critical temperature (\(T_c\)) of these structures. This involves the evaluation of key physical properties such as the electron - phonon coupling strength. ### Main solutions The paper proposes a three - step workflow to achieve the above goals: 1. **Identify cage - like frameworks**: Screen out framework structures suitable for forming cage - like hydrides from three databases (including experimental databases and prediction databases). 2. **Classify framework stability**: Classify the stability of these frameworks through high - throughput calculations and machine - learning models, and screen out dynamically stable structures. 3. **Estimate the superconducting critical temperature**: Use features such as electronic structure and hydrogen - hydrogen distance to establish a model for quickly estimating \(T_c\) to accelerate the discovery of high - temperature superconductors. ### Key achievements - The research discovered 14 new cage - like hydride frameworks, of which 7 frameworks exhibit a superconducting critical temperature exceeding 250 K under 300 GPa. - Two specific structures (P63/mmc - Li2NaH17 and P6/mmm - ThY2H24) are predicted to have superconducting properties close to room temperature under specific pressures, which are 297 K and 303 K respectively. - The proposed workflow significantly improves the screening efficiency and provides a powerful tool for the future exploration of high - temperature superconducting materials. Through this method, researchers can explore and predict high - temperature superconducting materials more systematically, laying the foundation for future synthesis and applications.

Data-driven design of high-temperature superconductivity among ternary hydrides under pressure

Novel Superconducting Ternary Hydrides under High Pressure

Designing ternary superconducting hydrides with A15-type structure at moderate pressures

Tuning Chemical Precompression: Theoretical Design and Crystal Chemistry of Novel Hydrides in the Quest for Warm and Light Superconductivity at Ambient Pressures

Superconducting ternary hydrides under high pressure

The systematic study on the phase diagram and superconductivity of ternary clathrate Ca−Sc−H at high pressures

Designing Quaternary Hydrides with Potential High T$_c$ Superconductivity

Superconducting ternary hydrides: progress and challenges

Pressure-induced hydride superconductors above 200 K

Generic Rules for Achieving Room-Temperature Superconductivity in Ternary Hydrides with Clathrate Structures

Prediction of Ambient Superconductivity in Ternary Thorium-Silicon Superhydrides with a Breathing Kagome Lattice

High-pressure synthesis of a ternary yttrium-sulfur hydride superconductor with a high Tc of approximately 235 K

Superconductive Sodalite-like Clathrate Hydrides MXH$_{12}$ with Critical Temperatures of near 300 K under Pressures

Design of superconducting compounds at lower pressure via intercalating XH molecules (X = B, C, and N) into fcc lattices

Formation and Superconducting Properties of Predicted Ternary Hydridescyh6under Pressures

Superconducting Ternary Hydrides in Ca-U-H under High Pressure

High-Te Superconductivity in Squeezed Cubic CSeH6 and C2TeH8 Ternary Polyhydrides

Computational design of new superconducting materials and their targeted experimental synthesis

Unlocking the Origin of High‐Temperature Superconductivity in Molecular Hydrides at Moderate Pressures

Pressure-induced high-temperature superconductivity in ternary Y-Zr-H compounds

Prediction of high- T c superconductivity in ternary lanthanum borohydrides