Abstract:The primary challenge in the field of high-temperature superconductivity in hydrides is to achieve a superconducting state at ambient pressure rather than the extreme pressures that have been required in experiments so far. Here, we propose a family of compounds, of composition Mg$_2$XH$_6$ with X$=$Rh, Ir, Pd, or Pt, that achieves this goal. These materials were identified by scrutinizing more than a million compounds using a machine-learning accelerated high-throughput workflow. They are thermodynamically stable, indicating that they are serious candidates for experimental synthesis. We predict that their superconducting transition temperatures are in the range of 45-80K, or even above 100K with appropriate electron doping of the Pt compound. These results indicate that, although very rare, high-temperature superconductivity in thermodynamically stable hydrides is achievable at room pressure.

What problem does this paper attempt to address?

The key problem that this paper attempts to solve is to achieve high - temperature superconductivity of hydrides at ambient pressure. Specifically, current research on high - temperature superconducting hydrides mainly focuses on extremely high - pressure conditions (such as over 100 GPa), which is extremely difficult in practical applications. Therefore, researchers hope to find materials that can exhibit high - temperature superconductivity at ambient pressure or close to ambient pressure. ### Core problems of the paper 1. **Achieving high - temperature superconductivity at ambient pressure**: At present, most high - temperature superconducting hydrides require extremely high pressure to exhibit superconducting properties, and these high - pressure conditions are very difficult to maintain in experiments and practical applications. Therefore, finding materials that can achieve high - temperature superconductivity at ambient pressure is one of the key challenges in this field. 2. **Thermodynamic stability**: Many predicted high - temperature superconducting materials are not stable at ambient pressure and are prone to decompose into other compounds, making experimental synthesis and characterization very difficult. Therefore, it is very important to find materials that have both high - temperature superconductivity and are thermodynamically stable at ambient pressure. ### Solutions in the paper The paper proposes a new class of compounds - Mg₂XH₆ (where X is Rh, Ir, Pd or Pt). These compounds may be thermodynamically stable at ambient pressure and may exhibit high - temperature superconductivity. Through a high - throughput screening method accelerated by machine learning, researchers screened these potential candidate materials from more than 1 million compounds. ### Prediction results - **Superconducting transition temperature**: It is predicted that the superconducting transition temperature (Tc) of these materials is between 45 - 80 K. Even with appropriate electron doping, the Tc of Pt compounds can exceed 100 K. - **Thermodynamic stability**: These compounds are thermodynamically stable at ambient pressure, indicating that they are ideal candidate materials for experimental synthesis. ### Conclusion This research provides a new direction for achieving high - temperature superconductivity at ambient pressure, especially for those materials that have both high - temperature superconductivity and are thermodynamically stable at ambient pressure. This finding provides important references and guidance for future superconducting material research and development.

Prediction of Ambient Pressure Conventional Superconductivity above 80K in Thermodynamically Stable Hydride Compounds

Prediction of ambient pressure conventional superconductivity above 80 K in hydride compounds

Searching Materials Space for Hydride Superconductors at Ambient Pressure

Feasible route to high-temperature ambient-pressure hydride superconductivity

Prediction of ambient pressure superconductivity in cubic ternary hydrides with MH$_6$ octahedra

Prediction of Room-Temperature Superconductivity in Quasi-atomic H2-Type Hydrides at High Pressure

Prediction of ambient pressure superconductivity in cubic ternary hydrides with MH6 octahedra

Prediction of Ambient Superconductivity in Ternary Thorium-Silicon Superhydrides with a Breathing Kagome Lattice

Computational Materials Discovery for Lanthanide Hydrides at high pressure: predicting High Temperature superconductivity

High-temperature Superconductivity in Sulfur Hydride Evidenced by Alternating-Current Magnetic Susceptibility

Pressure-induced hydride superconductors above 200 K

Ambient pressure high temperature superconductivity in RbPH$_3$ facilitated by ionic anharmonicity

Tuning Chemical Precompression: Theoretical Design and Crystal Chemistry of Novel Hydrides in the Quest for Warm and Light Superconductivity at Ambient Pressures

Prediction of high-<i>T<sub>c</sub></i> superconductivity in H<sub>6</sub>SX (<i>X</i> = Cl, Br) at pressures below one megabar

Theoretical Study of Stability and Superconductivity Ofschn(n=4–8) at High Pressure

Unlocking the Origin of High‐Temperature Superconductivity in Molecular Hydrides at Moderate Pressures

Future Study of Dense Superconducting Hydrides at High Pressure

High-pressure Phase Stability and Superconductivity of Pnictogen Hydrides and Chemical Trends for Compressed Hydrides

Synthesis of Mg$_2$IrH$_5$: A potential pathway to high-$T_c$ hydride superconductivity at ambient pressure

Hydrogen‐rich Superconductors at High Pressures