Abstract:Single crystals of XPt$_{5}$P (X = Al, Ga, and In) were grown from a Pt-P solution at high temperatures, and ambient-pressure measurements of temperature-dependent magnetization, resistivity, and X-ray diffraction were made. Also, the ambient-pressure Hall resistivity and temperature-dependent resistance under pressure were measured on GaPt$_{5}$P. All three compounds have tetragonal $P4/mmm$ crystal structure at room-temperature with metallic transport and weak diamagnetism over the $2-300$~K temperature range. Surprisingly, at ambient pressure, both the transport and magnetization measurements on GaPt$_{5}$P show a step-like feature in $70-90$~K region suggesting a possible structural phase transition, and no such features were observed in (Al/In)Pt$_{5}$P. Both the hysteretic nature and sharpness of the feature suggest the first-order transition, and single-crystal X-ray diffraction measurements provided further details of the structural transition with a crystal symmetry likely different than $P4/mmm$ below transition. The transition is characterized by anisotropic changes in the lattice parameters, a volume collapse, and satellite peaks at two distinct wave-vectors. Density functional theory calculations present phonon softening as a possible driving mechanism. Additionally, the structural transition temperature increases rapidly with increasing pressure, reaching room temperature by $\sim 2.2$~GPa, highlighting the high degree of pressure sensitivity and fragile nature of GaPt$_{5}$P room-temperature structure. Although the volume collapse and extreme pressure sensitivity suggest chemical pressure should drive a similar structural change in AlPt$_{5}$P, with smaller unit cell dimensions and volume, its structure is found to be $P4/mmm$ as well. Overall, GaPt$_{5}$P stands out as a sole member of the 1-5-1 family of compounds with a temperature-driven structural change.

What problem does this paper attempt to address?

The problem that this paper attempts to solve is about the first - order structural phase transition of GaPt_5P at low temperatures and its rapid enhancement phenomenon under pressure. Specifically: 1. **First - order structural phase transition**: The paper studied whether GaPt_5P would undergo a first - order structural phase transition at low temperatures. Through experimental means such as resistivity, magnetic susceptibility, and single - crystal X - ray diffraction, the authors found that GaPt_5P indeed has an obvious phase - transition feature in the temperature range of 70 - 90 K, manifested as step - like changes in resistance and magnetic susceptibility. This change has an obvious hysteresis effect, indicating that it is a first - order phase transition. 2. **Pressure sensitivity**: The paper further explored the sensitivity of this phase transition to pressure. The experimental results show that as the pressure increases, the phase - transition temperature rises rapidly, and at a pressure of about 2.2 GPa, the phase - transition temperature can reach room temperature. This indicates that the structural phase transition of GaPt_5P is very sensitive to pressure. 3. **Phase - transition mechanism**: In order to understand the mechanism of the phase transition, the authors carried out density - functional - theory (DFT) calculations and found that phonon softening at the wave vector (0.5, 0.5, 0.5) may be a key factor leading to the phase transition. In addition, the satellite peaks observed in the single - crystal X - ray diffraction experiment also support this conclusion. These satellite peaks indicate that the symmetry of the crystal has changed after the phase transition, forming a double - Q - type structure. 4. **Comparison with other compounds**: The paper also compared the properties of AlPt_5P and InPt_5P and found that these two compounds do not show similar phase - transition features in the same temperature range, thus highlighting the uniqueness of GaPt_5P. In summary, the main objective of this paper is to reveal the first - order structural phase - transition phenomenon of GaPt_5P at low temperatures and its sensitivity to pressure, and to explore the underlying physical mechanism through various experimental means and theoretical calculations.

The first-order structural phase transition at low-temperature in GaPt$_{5}$P and its rapid enhancement with pressure

Phase Transition in PbTiO3 under Pressure Studied by the First-Principles Method

New Exploration on Phase Transition and Structure of PbS under High Pressure and Temperature

Pressure-Induced Reversible Hcp to Fcc Phase Transition of Ti: A First-Principles Study

Structural, magnetic and insulator-to-metal transitions under pressure in the GaV4S8 Mott insulator: A rich phase diagram up to 14.7 GPa

High-pressure Structural Phase Transition and Metallization in Ga2S3 under Non-Hydrostatic and Hydrostatic Conditions Up to 36.4 GPa

Phase transition of intermetallic TbPt at high temperature and high pressure.

High pressure ferroelastic phase transition in SrTiO3

Pressure-induced Reversible Phase Transition on Mo2Ga2C

Structure Evolution, Elastic And Electronic Properties Of Pt-Doped Ti Alloy Under Pressure

Elemental Phosphorus: structural and superconducting phase diagram under pressure

Pressure-Induced Phase Transitions of Ax(2)-Type Iron Pnictides: an Ab Initio Study

Near-room-temperature ferromagnetic ordering in the pressure-induced collapsed-tetragonal phase in SrCo2P2

Pressure-induced Metallization in the Absence of a Structural Transition in the Layered Ferromagnetic Insulator Cr2Ge2Te6

Electronic structure and photoconductivity properties of GaP under high pressure

Structural, mechanical, thermodynamic and electronic properties of Pt3M (M = Al, Co, Hf, Sc, Y, Zr) compounds under high pressure

Raman spectroscopy study of pressure-induced phase transitions in single crystal CuInP2S6

Highly Responsive Ground State of PbTaSe_2: Structural Phase Transition and Evolution of Superconductivity under Pressure

Evolution of Structural and Electronic Properties of TiSe2 under High Pressure

Pressure-induced Phase Transition of Lead Phosphate Pb3(PO4)2: X-ray Diffraction and XANES