Phase transition of intermetallic TbPt at high temperature and high pressure.

Fei Qin,Xiang Wu,Ke Yang,Shan Qin
DOI: https://doi.org/10.1088/1361-648X/aaaf9b
2018-01-01
Abstract:Here we present synchrotron-based x-ray diffraction experiments combined with diamond anvil cell and laser heating techniques on the intermetallic rare earth compound TbPt (Pnma and Z = 4) up to 32.5 GPa and similar to 1800 K. The lattice parameters of TbPt exhibit continuous compression behavior up to 18.2 GPa without any evidence of phase transformation. Pressure-volume data were fitted to a third-order Birch-Murnaghan equation of state with V-0 = 175.5(2) angstrom(3), K-T0 = 110(5) GPa and K-T0 = 3.8(7). TbPt exhibits anisotropic compression with ss(a) > ss(b) > ss(c) and the ratio of axial compressibility is 2.50:1.26:1.00. A new monoclinic phase of TbPt assigned to the Pc or P2/c space group was observed at 32.5 GPa after laser heating at similar to 1800 K. This new phase is stable at high pressure and presented a quenchable property on decompression to ambient conditions. The pressure-volume relationship is well described by the second-order Birch-Murnaghan equation of state, which yields V-0 = 672(4) angstrom(3), K-T0 = 123(6) GPa, which is about similar to 14% more compressible than the orthorhombic TbPt. Our results provide more information on the structure and elastic property view, and thus a better understanding of the physical properties related to magnetic structure in some intermetallic rare earth alloys.
What problem does this paper attempt to address?