Abstract:As tellurides and selenides of Bismuth are extensively used thermoelectric materials in the low-temperature range with refrigeration application, A concerted effort is put forth to boost the ZT by co-doping the pristine Bi 2 Se 3 with antimony (Sb) on cation end and tellurium (Te) on anion side of the compound. The double sintered solid-state reaction method is employed in the preparation of Bi 2 Se 3 and (Bi 1− x Sb x ) 2 Se 2.7 Te 0.3 polycrystalline pellets, with x = 0.02, 0.04, and 0.06. The sample exhibits a rhombohedral structure with the space group of R m. FESEM and EDAX analysis are used to confirm surface morphology and elemental composition of the produced samples. The thermoelectric measurements for the pristine and co-doped samples were conducted by the physical property measurement system as well as a considerable increase in the Seebeck coefficient of − 115 μV/K is observed for 0.02 doping of the Sb which is 4.2 times greater than as for pristine (S = − 28 μV/K). Higher concentration doping ( x = 0.04, 0.06) has not reflected any Seebeck coefficient advancement. In contrast, the lowest total thermal conductivity at a low-temperature regime (< 50 K) is observed for x = 0.06 doping concentration which at near room temperature increases beyond the pristine thermal conductivity; whereas, x = 0.02, 0.04 doping concentration shows a decrement in total thermal conductivity at low, at room temperature region the values are almost equivalent to that of pristine. The co-doped samples' electrical resistivity is substantially less than pristine sample. The highest power factor of 3 × 10 –4 μW/mK 2 is obtained for the x = 0.02 sample. The highest ZT value for the x = 0.02 sample is almost 28 times more than a pristine sample. We conducted a study where we combined experimental and DFT methods to investigate thermoelectric properties incorporated into pristine and doped with antimony and tellurium on Bi 2 Se 3 . We have employed this combination to investigate the partial density of states, Seebeck coefficient, power factor using the Boltzmann transport equation. Theoretical thermoelectric data were derived and compared to experimental observations. Hence, using combined experimental and theoretical investigations helps to predict with higher accuracy of thermoelectric properties of semiconducting materials.

Thermoelectric properties of marcasite-type compounds MSb$_2$ (M = Ta, Nb): A combined experimental and computational study

The transport properties of Nb-doped trichalcogenide Ta0.8Nb0.2S3

A comprehensive experimental and DFT analysis on thermoelectric properties of Sb, Te co-doped Bi2Se3 polycrystals

Enhanced Thermoelectric Performance of $p$-type BiSbTe Through Incorporation of Magnetic CrSb

Thermoelectric transport properties of CaMg2Bi2, EuMg2Bi2, and YbMg2Bi2

Cooperative regulation of electrical and thermal transport behavior enhancing the thermoelectric performance of SnTe

Transport and Thermoelectric Properties of Sr-3(Ti0.95r0.05)(2)O-7 (R = Ta, Nb, W) Oxides

Thermoelectric Transport in Weyl Semimetal BaMnSb2: a First-Principles Study

Thermoelectric Properties of Novel Semimetals: A Case Study of YbMnSb2

Thermoelectric response of textured Sb2Te3–BiSb and Sb2Te3–Bi2Te3 thin film junctions

Thermoelectric Transport Properties of CaMg2Bi2, EuMg2Bi

High Power Factor and Thermoelectric Figure of Merit in Sb 2 Si 2 Te 6 through Synergetic Effect of Ca Doping

Band Engineering and Phonon Engineering Effectively Improve N-Type Mg3Sb2 Thermoelectric Material Properties.

Thermoelectric Properties of Nanocrystalline (mg1−xznx)3sb2isostructural Solid Solutions Fabricated by Mechanical Alloying

Thermoelectric Performance of Binary Lithium-Based Compounds: Li3Sb and Li3Bi

Effect of electron-phonon scattering, pressure and alloying on the thermoelectric performance of TmCu$_3$Ch$_4$ (Tm=V, Nb, Ta; Ch=S, Se, Te)

Large Thermoelectric Power Factor in One-Dimensional Telluride Nb4SiTe4 and Substituted Compounds

Enhanced Thermoelectric Performance of CuSbSe2 Via Mn Doping

Na/Bi-co-doping and Heterogeneous Interfaces Leading to Enhanced Thermoelectric Performance of P-Type Mg3Sb2-based Zintls

Extraordinary Thermoelectric Performance in N-Type Manganese Doped Mg3Sb2 Zintl: High Band Degeneracy, Tuned Carrier Scattering Mechanism and Hierarchical Microstructure

Two-dimensional BiSbTeX2 (X = S, Se, Te) and their Janus monolayers as efficient thermoelectric materials