Improved understanding of the growth of blocky alpha in welded Zircaloy-4

Ruth M. Birch,T. Ben Britton

2024-02-27

Abstract:Zirconium alloys are widely used in nuclear reactors as fuel cladding materials. Fuel cladding is used to contain the nuclear fuel and cladding tubes are typically sealed using welds. Welding of zirconium alloys can result in changes in the local microstructure, with the potential to grow so called 'blocky {\alpha}' grains in the welded region during subsequent thermal processing and these blocky {\alpha} grains have the potential to be detrimental to the integrity of the component. In this work, complimentary heating experiments with ex situ and in situ electron backscatter diffraction (EBSD) analysis are used to aid understanding of the blocky {\alpha} grain growth within the weld region. These experiments reveal that blocky {\alpha} grain growth is related to the parent \b{eta} (high temperature) microstructure, as grains grow adjacent to a prior \b{eta} grain boundary and the orientation of the growing {\alpha} grain can be explained using neighbourhood orientations from this prior \b{eta} grain. This growth mechanism is explained via a simple mechanism which is related to the {\alpha} grain orientations, grain boundary structures and local stored energy. Ultimately, our findings indicate that the likely grain growth (size and morphology) across the weld region can now be predicted from the initial as-welded microstructure.

Materials Science

What problem does this paper attempt to address?

### Problems the Paper Attempts to Solve

The paper aims to address the issue of "blocky α" grain growth in Zircaloy-4 alloy during the welding process. Specifically, the welding process can lead to changes in the local microstructure, particularly during subsequent heat treatment, where the welded area may form so-called "blocky α" grains. These "blocky α" grains can adversely affect the integrity of components, especially in thin-walled components where the grain size may approach the wall thickness, thus impacting the performance of the components.

### Background and Research Motivation

Zirconium alloys (such as Zircaloy-4) are widely used as fuel cladding materials in nuclear reactors. To maintain and optimize the performance of these materials, their microstructure is strictly controlled during manufacturing. However, welding operations can lead to changes in the local microstructure, particularly post-electron beam welding heat treatment, which may result in abnormal grain growth forming "blocky α" grains. The formation of these grains not only changes the grain boundary density but also significantly alters the local crystallographic texture, potentially affecting the performance of the components.

### Research Methods

To understand the growth mechanism of "blocky α" grains, the authors conducted the following experiments:

1. **In-situ Heating Experiments**: Observing the initial stages of grain growth by heating the sample under an electron microscope.
2. **Ex-situ Heating Experiments**: Heating the sample to a specific temperature and holding it for a period, then cooling it down and analyzing the microstructure.
3. **Electron Backscatter Diffraction (EBSD) Analysis**: Reconstructing the high-temperature β phase microstructure using EBSD technology and comparing it with the low-temperature α phase microstructure.

### Main Findings

1. **Regions of Grain Growth**: Grain growth was observed throughout the welded area, particularly in the heat-affected zone (HAZ) and the fusion zone (FZ).
2. **Relationship with Prior β Phase Microstructure**: By reconstructing the prior β phase microstructure, it was found that the growth of "blocky α" grains is related to the grain boundaries of the prior β phase, rather than growing from the α variants within the prior β phase.
3. **Growth Mechanism**: Grains grow outward from one prior β phase domain to the adjacent β phase domain, and the growth direction is related to the orientation of the neighboring β phase domain. Grains tend to grow from low stored energy regions to high stored energy regions, consistent with the strain-induced boundary migration (SIBM) mechanism.
4. **Influencing Factors**: Grain growth is influenced by multiple factors, including the intersections of α lamellae, long straight grain boundaries, and the distribution of local strain energy.

### Conclusion

Through these experiments, the authors proposed a method to predict the final microstructure of the welded area. This finding helps optimize the welding process, reducing the formation of "blocky α" grains, thereby improving the performance and safety of nuclear reactor fuel cladding materials.