Abstract:Optimized shape anisotropy of the Fe-Co rich ferromagnetic (α 1 ) phase and the effective separation of the α 1 and α 2 phases with maximum magnetization difference—where α 2 represents a paramagnetic magnetic phase—are the key parameters for maximizing the magnetic properties of Alnico magnets. In this manuscript, efforts have been undertaken to optimize the shape anisotropy of the α 1 phase and increase the difference in magnetization and separation between α 1 and α 2 phases by fine tuning Al and Ni contents, directional solidification and magnetic field annealing methods. At first, Alnico magnets were fabricated by adjusting the content of α 2 phase followed by homogenization, magnetic field annealing at high temperature, and low-temperature tempering. Intrinsic coercivity ( H cj ) of ⁓146.0 kA/m, remanence ( B r ) of ⁓0.90 T and maximum energy density ( (BH) max ) of 46.02 kJ/m 3 are achieved in the magnet with 8.2 wt% Al and 12.8 wt% Ni treated in field of 1.5 T for 10 minutes. At the second stage, the magnet with optimal magnetic properties is directionally solidified to develop columnar grains, and then the α 1 phase is grown in the direction of the columnar grains by magnetic field annealing to enhance the (BH) max to 79.8 kJ/m 3 . The axial ratio of the α 1 phase increased significantly with the increase of the grain size, particularly in the directionally solidified magnets. The Curie temperature of the α 1 phase is noted near 1150 K, while the Curie temperature of the α 2 phase is below 400 K. The magnets demonstrated excellent temperature stability, with magnetic properties decreasing by only 10–12 % at 800 K. These results may pave the way for further development of Alnico magnets specifically for high temperature applications.

Multistep severe plastic deformation to achieve non-rare earth bulk magnets with high α-MnBi phase content

Multistep severe plastic deformation to achieve non-rare earth bulk magnets with high α-MnBi phase content

Synthesis of hard magnetic α-MnBi phase by high pressure torsion and field assisted annealing

Phase Evolution, Microstructure and Magnetic Properties of Bulk Α-Fe/nd2fe14b Nanocomposite Magnets Prepared by Severe Plastic Deformation and Thermal Annealing

Tuning the Microstructure and Magnetic Properties of Bulk Nanocomposite Magnets with Large Strain Deformation

Construction of High-Performance Multi-Main-phase Nd–Dy–Fe–B Sintered Magnets with Strengthened Chemical Heterogeneity

Engineering microstructure to improve coercivity of bulk MnBi magnet

Simultaneously Increasing the Magnetization and Coercivity of Bulk Nanocomposite Magnets Via Severe Plastic Deformation

A Reliable Route for Relieving the Constraints of Multi-Main-phase Nd–La–Ce–Fe–B Sintered Magnets at High La–Ce Substitution: (pr, Nd)H Grain Boundary Diffusion

Defect manipulation for the coercivity enhancement of Nd-Fe-B permanent magnets

Manufacturing of Textured Bulk Fe-SmCo$_{5}$ Magnets by Severe Plastic Deformation

Bulk Α-Fe/nd2fe14b Nanocomposite Magnets Produced by Severe Plastic Deformation Combined with Thermal Annealing

Anisotropic bulk rare-earth-free Mn-Al-(C) magnets prepared under high-stress and large-strain conditions

Bulk Anisotropic Nd2fe14b/Alpha-Fe Nanocomposite Magnets Prepared By Hot-Deformation Processing Of Amorphous Alloys

Magnetic-field-induced transformation and strain in polycrystalline FeMnGa ferromagnetic shape memory alloys with high cold-workability

Bulk α-Fe/Nd2Fe14B nanocomposite magnets prepared by hot deformation of amorphous Nd10.5Fe82Cu 1.5B6

Banded-like Morphology and Martensitic Transformation of Dual-Phase Ni–Mn–In Magnetic Shape Memory Alloy with Enhanced Ductility

Tuneable Magneto-Resistance by Severe Plastic Deformation

Achieving Ultrastrong Anisotropy in Bulk Pr2Fe14B/α-Fe Nanocomposite Magnets by High-Pressure Thermal Compression

Grain boundary restructuring of multi-main-phase Nd-Ce-Fe-B sintered magnets with Nd hydrides

Refining Alnico 8 magnets with composition optimization of matrix phase, directional solidification and magnetic field annealing