Abstract:Environmental barrier coatings (EBCs) enable SiCf/SiC ceramic matrix composites (CMC) to operate under high-temperature combustion conditions. They reduce the oxidation rate of SiC f/SiC, the volatilization of the composites due to reaction with water vapor, and the surface temperature of the composites. Rare-earth monosilicates (RE2SiO5), owing to their excellent high-temperature durability, low thermal conductivity, and good phase stability, are used as the top layer of EBCs. However, they exhibit a high coefficient of thermal expansion (CTE), leading to thermal mismatch and inducing tensile residual stress (with a magnitude of several hundred MPa) in the coating, resulting in the formation of vertical cracks, which act as extremely-high-diffusivity paths for oxidation species transportation and silica volatilization. Therefore, regulating the CTE of RE2SiO5 EBCs and minimizing the CTE mismatch among constituent RE2SiO5 layers with SiC f/SiC CMCs are critical for multilayered EBCs. Through atmospheric plasma spraying, a typical Yb2SiO5/Yb 2Si2O7/Si coating system and a tri-layer structured multicomponent (Y1/4Ho1/4Er1/4Yb1/4)(2)SiO5/Yb2Si2O7/Si coating system with better matched CTEs were manufactured. Both the coatings remained adhered to the substrate during deposition and after annealing, and no mud cracks that would compromise the coating gas-tightness quality and delamination cracks were observed at any of the coating interfaces. In thermal cycling tests, (Y1/4Ho1/4Er1/4Yb1/4)(2)SiO5/Yb2Si2O7/Si coatings showed a lifetime that is three times longer than that of conventional Yb2SiO5/Yb2Si2O7/Si coatings. The failure mechanisms in thermal cycling were investigated via the finite element simulation of stress. It was found that the stress in the substrate was low, and the residual thermal stress was mainly concentrated on the top, inter, and bond layers and increased with an increase in temperature. Compared with that of the (Y1/4Ho1/4Er1/4Yb1/4)(2)SiO5 top coat, the Yb2SiO5 top coat showed obviously higher residual tensile stress, which contributed to a higher tendency for mud-crack formation and higher energy release rate, substantially reducing the coating.. s thermal cycling lifetime. Through neutron powder diffraction and pair distribution function (PDF) analysis, the average and local structures of RE2SiO5 were studied. Overall, the average and local structures did not differ significantly, both of which can be described using the C2/c structure. Nevertheless, the PDF results demonstrated some differences in the disorder degree of Si-O and RE-O coordination environments. In particular, Rietveld refinement results of the PDF showed lower local distortion degree of [ORE4] tetrahedrons when compared with that of the average structure. It is effective to reduce the distortion degree of [ORE4] tetrahedrons by introducing Y3+, Ho3+, and Er3+ into the Yb3+ sites of Yb2SiO5, and smaller distortion degrees lead to lower CTE values. Coordinative local disturbances introduced by strategic high-entropy design have been proposed as the key method for CTE regulation.

Improved thermophysical properties of rare-earth monosilicates applied as environmental barrier coatings by adjusting structural distortion with RE-doping

Improved thermal properties and CMAS corrosion resistance of rare-earth monosilicates by adjusting the configuration entropy with RE-doping

Towards Thermal Barrier Coating Application for Rare Earth Silicates RE2SiO5 (RE = La, Nd, Sm, Eu, and Gd)

First-principles calculations and thermal-mechanical experimental studies on middle-entropy rare-earth disilicates

Contributions of bonding heterogeneity to mechanical and thermal properties of rare earth molybdates for thermal barrier coatings

Thermal performance regulation of high‐entropy rare‐earth disilicate for thermal environmental barrier coating materials

Composition Effects on Elastic, Thermal and Corrosion Properties of Multiple-Re Silicate (ho1/4er1/4yb1/4lu1/4)2sio5 As a Promising Thermal and Environmental Barrier Coating Material

Enhanced High-Temperature Performance of Selected High-entropy Rare Earth Disilicates

(Ho0.25Lu0.25Yb0.25Eu0.25)2SiO5 high-entropy ceramic with low thermal conductivity, tunable thermal expansion coefficient, and excellent resistance to CMAS corrosion

High-entropy rare-earth disilicate (Lu0.2Yb0.2Er0.2Tm0.2Sc0.2)2Si2O7: A potential environmental barrier coating material

Design rules for the thermal and elastic properties of rare-earth disilicates

(Sm0.2Eu0.2Tb0.2Dy0.2Lu0.2)2Si2O7: A novel high-entropy rare earth disilicate porous ceramics with high porosity and low thermal conductivity

Neutron Pair Distribution Function Analysis to the Local Structure of High-Entropy RE2SiO5 Environmental Barrier Coating

Pronounced Enhancement of Thermal Expansion Coefficients of Rare-Earth Zirconate by Cerium Doping

Potential thermal barrier coating material: High entropy ceramic (Ca0.5Sr0.5)(5RE)2O4 with enhanced thermophysical properties

Improved thermal properties and CMAS corrosion resistance of high-entropy RE zirconates by tuning fluorite-pyrochlore structure

High‐entropy rare earth titanates with low thermal conductivity designed by lattice distortion

A Novel Strategy to Obtain High-Entropy (5re0.2)2si2o7 with Excellentcalcium-Magnesium-Aluminosilicate Corrosion Resistance

Thermal properties of high-entropy RE-disilicates controlled by high throughput composition design and optimization

Phase evolution and thermophysical properties of high-entropy RE<sub>2</sub>(Y<sub>0.2</sub>Yb<sub>0.2</sub>Nb<sub>0.2</sub>Ta<sub>0.2 </sub>Ce<sub>0.2</sub>)<sub>2</sub>O<sub>7</sub> oxides

An extremely low thermal conduction ceramic: RE 9.33(SiO 4) 6O 2 silicate oxyapatite