Atomistic origins of asymmetric charge-discharge kinetics in off-stoichiometric LiNiO$_2$

Penghao Xiao,Ning Zhang,Harold Smith Perez,Minjoon Park

DOI: https://doi.org/10.1021/acs.chemmater.3c03228

2023-11-10

Abstract:LiNiO$_2$ shows poor Li transport kinetics at the ends of charge and discharge in the first cycle, which significantly reduces its available capacity in practice. The atomistic origins of these kinetic limits have not been fully understood. Here, we examine Li transport in LiNiO$_2$ by first-principles-based kinetic Monte Carlo simulations where both long time scale and large length scale are achieved, enabling direct comparison with experiments. Our results reveal the rate-limiting steps at both ends of the voltage scan and distinguish the differences between charge and discharge at the same Li content. The asymmetric effects of excess Ni in the Li layer (Ni$_\textrm{Li}$) are also captured in our unified modelling framework. In the low voltage region, the first cycle capacity loss due to high overpotential at the end of discharge is reproduced without empirical input. While the Li concentration gradient is found responsible for the low overpotential during charge at this state of charge. Ni$_\textrm{Li}$ increases the overpotential of discharge but not charge because it only impedes Li diffusion in a particular range of Li concentration and does not change the equilibrium voltage profile. The trends from varying the amount of Ni$_\textrm{Li}$ and temperature agree with experiments. In the high voltage region, charge becomes the slower process. The bottleneck becomes moving a Li from the Li-rich phase (H2) into the Li-poor phase (H3), while the Li hopping barriers in both phases are relatively low. The roles of preexisting nucleation sites and Ni$_\textrm{Li}$ are discussed. These results provide new atomistic insights of the kinetic hindrances, paving the road to unleash the full potential of high-Ni layered oxide cathodes.

Materials Science

What problem does this paper attempt to address?

### Problems Addressed by the Paper

This paper aims to explore the atomic origins of asymmetric kinetic limitations during the charge and discharge processes in non-stoichiometric lithium nickel oxide (LiNiO₂). Specifically, the paper focuses on the following points:

1. **Kinetic Limitations in the Low Voltage Region**:
- At the end of the first charge-discharge cycle, LiNiO₂ exhibits poor lithium transport kinetics, significantly reducing its practically usable capacity.
- Through first-principles-based Monte Carlo simulations (KMC), researchers reveal the high overpotential phenomenon at the end of discharge in the low voltage region (around 3.0 V), which is the main cause of the first cycle irreversible capacity loss (IRC).
- The study finds that the lithium concentration gradient plays an important role in the low overpotential during the charging process.

2. **Impact of Ni in the Lithium Layer**:
- The presence of excess nickel (Ni Li) in the lithium layer increases the overpotential during discharge but has a smaller impact on charging. This is because Ni Li only hinders lithium diffusion within a specific lithium concentration range without altering the equilibrium voltage curve.
- By adjusting the content of Ni Li and temperature, the research results are consistent with experimental data.

3. **Kinetic Limitations in the High Voltage Region**:
- In the high voltage region (around 4.4 V), charging becomes a slower process. The bottleneck lies in moving lithium from the lithium-rich phase (H2) to the lithium-poor phase (H3), while the lithium hopping barriers in both phases are relatively low.
- The roles of pre-existing nucleation sites and Ni Li are discussed.

### Summary

Through multi-scale modeling and experimental validation, this paper delves into the kinetic limitations and their atomic origins during the charge and discharge processes of LiNiO₂. These findings provide new atomic-level insights for understanding and optimizing high-nickel layered oxide cathode materials, helping to unlock the full potential of these materials.