Capacity Decay in LiNiO2: An Atomistic Kinetic Picture

Penghao Xiao
DOI: https://doi.org/10.26434/chemrxiv-2024-fq0qb
2024-10-08
Abstract:High-Ni layered oxides experience significant capacity decay over cycling, but the underlying mechanisms remain controversial. Using atomistic simulations, the electrochemical behavior of the fatigue phase is reproduced: a surface densified phase traps the last 25% of Li the end of charge, while discharge remains unimpeded. When the Li content falls to 25%, the remaining Li are locked into a superlattice, making the creation of vacancies the rate-limiting step for further delithiation. After cycling, the surface densified phase resembles Ni5O8 , with 25% Ni in the Li layer forming a similar superlattice. These Ni pin nearby Li, suppressing vacancy formation at the surface and kinetically trapping Li inside. Meanwhile, the Ni5O8 phase exhibits high diffusivity for Li interstitials in the superlattice, which explains the minimal resistance increase during discharge at the same Li content. Further densification leads to a surface phase that hinders both charge and discharge across the entire voltage range.
Chemistry
What problem does this paper attempt to address?
The paper aims to address the issue of capacity degradation in high-nickel layered oxides (such as LiNiO2) during cycling. Specifically, the authors investigate how surface dense phases (such as the β-phase Ni5O8) affect the delithiation process of lithium ions through atomic-scale kinetic simulations, and explain why the last 25% of lithium gets locked at the end of charging, while this phenomenon is not significant during discharging. The main findings include: 1. **Lithium Ion Trapping**: The surface β-phase (Ni5O8) traps the last 25% of lithium, but still remains conductive for the transport of other lithium ions. 2. **Kinetic Trap**: The β-phase strongly fixes the nearby lithium ions, preventing the formation of lithium interstitial-vacancy pairs, thereby inhibiting the nucleation of the H3 phase. 3. **Increased Resistance**: At high voltage, this trapping leads to an increase in charging overpotential, but the resistance increase is not significant during discharging. These findings help to understand the degradation mechanisms of high-nickel layered oxides during cycling and provide a theoretical basis for developing new surface modification strategies.