Understanding and unlocking the role of V in boosting the reversible hydrogen storage performance of MgH2
Yang Meng,Jian Zhang,Shunlong Ju,Yaxiong Yang,Zhenglong Li,Fang Fang,Dalin Sun,Guanglin Xia,Hongge Pan,Xuebin Yu
DOI: https://doi.org/10.1039/d3ta01029e
IF: 11.9
2023-04-29
Journal of Materials Chemistry A
Abstract:Although MgH 2 is widely regarded as one of the most promising solid-state hydrogen storage materials, the high operating temperature and sluggish kinetics of hydrogenation and dehydrogenation are major challenges for its practical application. Herein, V 6 O 13 nanobelts with a thickness of 11 nm are fabricated to promote the reversible hydrogen storage performance of MgH 2 . The favorable interaction between V 6 O 13 nanobelts and MgH 2 leads to in situ homogeneous formation of metallic V during the initial dehydrogenation of MgH 2 . Induced by the catalysis of metallic V, which results in weaker structural stability and higher surface states of MgH 2 attributed to the strong bonding interactions between V and H, the energy required for H 2 desorption from MgH 2 is decreased to 49.5 kJ mol −1 , 10.9 kJ mol −1 lower than that of pristine MgH 2 . Moreover, during the reversible hydrogenation process, the catalysis of metallic V lowers the energy for H 2 adsorption and dissociation on Mg down to −5.904 and 0.023 eV, respectively, while those values reach −0.086 and 1.103 eV for pristine Mg. As a result, with the introduction of V 6 O 13 nanobelts with an ultralow content of 3 wt%, a systematic hydrogen storage capacity of 6.8 wt% could be retained at 250 °C after 10 cycles.
materials science, multidisciplinary,chemistry, physical,energy & fuels