Haizhen Liu,Chenglin Lu,Xinchun Wang,Li Xu,Xiantun Huang,Xinhua Wang,Hua Ning,Zhiqiang Lan,Jin Guo

DOI: https://doi.org/10.1021/acsami.0c23150

2021-03-15

Abstract:Two-dimensional vanadium carbide (V₂C) and titanium carbide (Ti₃C₂) MXenes were first synthesized by exfoliating V₂AlC or Ti₃AlC₂ and then introduced jointly into magnesium hydride (MgH₂) to tailor the hydrogen desorption/absorption performances of MgH₂. The as-prepared MgH₂–V₂C–Ti₃C₂ composites show much better hydrogen storage performances than pure MgH₂. MgH₂ with addition of 10 wt % of 2V₂C/Ti₃C₂ initiates hydrogen desorption at around 180 °C; 5.1 wt % of hydrogen was desorbed within 60 min at 225 °C, while 5.8 wt % was desorbed within 2 min at 300 °C. Under 6 MPa H₂, the dehydrided MgH₂–2V₂C/Ti₃C₂ can start to recover hydrogen at room temperature, and 5.1 wt % of H₂ is obtained within 20 s at a constant temperature of 40 °C. The reversible capacity (6.3 wt %) does not decline for up to 10 cycles, which shows excellent cycling stability. The addition of 2V₂C/Ti₃C₂ can remarkably lower the activation energy for the hydrogen desorption reaction of MgH₂ by 37% and slightly reduce the hydrogen desorption reaction enthalpy by 2 kJ mol^–1 H₂. It was demonstrated that the combination of V₂C and Ti₃C₂ promotes the hydrogen-releasing process of MgH₂ compared with addition of only V₂C or Ti₃C₂, while Ti₃C₂ impacts MgH₂ more significantly than V₂C in the hydrogen absorption process of MgH₂ at ambient temperatures. A possible mechanism in the hydrogen release and uptake of the MgH₂–V₂C–Ti₃C₂ system was proposed as follows: hydrogen atoms or molecules may preferentially transfer through the MgH₂/V₂C/Ti₃C₂ triple-grain boundaries during the desorption process and through the Mg/Ti₃C₂ interfaces during the absorption process. Microstructure studies indicated that V₂C and Ti₃C₂ mainly act as efficient catalysts for MgH₂. This work provides an insight into the hydrogen storage behaviors and mechanisms of MgH₂ boosted by a combination of two MXenes.The Supporting Information is available free of charge at <a class="ext-link" href="/doi/10.1021/acsami.0c23150?goto=supporting-info">https://pubs.acs.org/doi/10.1021/acsami.0c23150</a>.XRD patterns of as-milled samples (Figure S1); XRD patterns of MgH₂ + 45 wt % (2V₂C/Ti₃C₂) in different states (Figure S2); isothermal hydrogen desorption curves; JMA plots; and Arrhenius's plots of as-milled samples (Figures S3–S6) (<a class="ext-link" href="/doi/suppl/10.1021/acsami.0c23150/suppl_file/am0c23150_si_001.pdf">PDF</a>)This article has not yet been cited by other publications.

materials science, multidisciplinary,nanoscience & nanotechnology