Improved Hydrogen Storage Properties of Li-Mg-N-H System by Lithium Vanadium Oxides

Hang Che,Yuhao Wu,Xinhua Wang,Haizhen Liu,Mi Yan

DOI: https://doi.org/10.1016/j.jallcom.2022.167603

IF: 6.2

2022-01-01

Journal of Alloys and Compounds

Abstract:The Mg(NH2)2-2LiH system is considered as one of the most potential hydrogen storage materials due to its high hydrogen storage capacity (5.6 wt%) and excellent reversible hydrogen adsorption and desorption performance. However, its poor kinetic characteristics of hydrogen absorption and desorption limit its practical application. In this work, Li3VO4 @LiVO2 was synthesized by a hydrothermal method, and was then introduced into Mg(NH2)2-2LiH system to enhance the hydrogen absorption and desorption kinetic char-acteristics. The results show that the hydrogen storage properties were greatly improved with addition of 10 wt% Li3VO4 @LiVO2 addition. As for the hydrogen absorption and desorption kinetics, the average hy-drogen absorption rate of 10 wt% Li3VO4 @LiVO2 modified Li-Mg-N-H sample within 20 min at 200 degrees C in-creased by 95.2% compared with that of the pristine Li-Mg-N-H sample, and the average hydrogen desorption rate of 10 wt% Li3VO4 @LiVO2 modified sample within 30 min at 180 degrees C increased by 42% compared with that of the pristine sample. The Ea of hydrogen desorption decreased from 117.86 kJ/mol to 99.43 kJ/mol, which also indicates that Li3VO4 @LiVO2 catalyst effectively improved the kinetic performance of hydrogen desorption and desorption of Li-Mg-N-H. Moreover, the hydrogen desorption capacity and hydrogen absorption capacity of 10 wt% Li3VO4 @LiVO2 modified Li-Mg-N-H increased by 18.4% and 13.8% compared with that of the pristine sample. The catalytic mechanism of Li3VO4 @LiVO2was discussed based on XRD, XPS and FTIR analysis results.(c) 2022 Elsevier B.V. All rights reserved.