Abstract:A novel Na2SO4@SiO2@Al2O3-SiO2 phase change material doped aerogel composite (PDAC) using the sol-gel technique is prepared. This new kind of composite material is composed of a core-shell structured Na2SO4@SiO2 phase change material (PCM) with high melting temperature and Al2O3-SiO2 aerogel with high thermal resistance and low thermal conductivity. The effects of PCM amounts and heat treatment temperatures on the physicochemical properties of Na2SO4@SiO2@Al2O3-SiO2 PDCA are investigated. X-ray diffraction (XRD) shows that when the mass percentage of Na2SO4@SiO2 PCM powders increases to 36.7%, the peaks corresponding to Na2SO4 can be well observed. The boehmite phase within Na2SO4@SiO2@Al2O3-SiO2 PDAC can be transformed to gamma-Al2O3 via structural adjustment after heat treatment at 600 *degrees C. The pore size distribution doesn't shift after 600*degrees C heat treatment, and the most probable pore diameter is at around 30 nm. Transmission Electron Microscopy (TEM) shows that the Na2SO4@SiO2 PCM powders with diameters at around 500 nm can be effectively trapped and are homogeneously distributed within the aerogel matrix even after further heat treatment at 1000*degrees C, therefore, liquid leakage can be inhibited during melting process. The peak latent heat of Na2SO4@SiO2@Al2O3-SiO2 PDCA can be as high as 153.84 J/g with the PCM mass percentage at 36.7%. The Brunauer-Emmett-Teller (BET) specific surface area increases from 419.3 m(2)/g to 630.6 m(2)/g due to structural adjustment, and then decreases to 277.7 m(2)/g caused by volume shrinkage. Thermal simulation results show that the total melting time can be 254.8 s, and development of the temperature distribution keeps well with that of the liquid fraction. The velocity distribution of the liquid PCM keeps at 0 due to the constraint of aerogel matrix. This Na2SO4@SiO2@Al2O3-SiO2 PDAC can be a promising high temperature PCM in thermal energy storage applications.

Hydrophobic modification of silica/exfoliated graphite nanoplatelets aerogel and its application as supporting material for form-stable phase change materials

Form-stable phase change material embedded with chitosan-derived carbon aerogel

Preparation and characterization of capric-palmitic acids eutectics/silica xerogel/exfoliated graphite nanoplatelets form-stable phase change materials

Investigation on thermal energy storage characteristics of form-stable phase change materials supported by graphene aerogel

Erythritol Confined in Multiwalled Carbon Nanotubes Reinforced Silica Aerogel As Novel Form-Stable Phase Change Materials

A promising form-stable phase change material composed of C/SiO2 aerogel and palmitic acid with large latent heat as short-term thermal insulation

Silica-based aerogels encapsulate organic/inorganic composite phase change materials for building thermal management

Engineering nanocellulose/graphene hybrid aerogel for form-stable composite phase change materials with high phase change enthalpy for energy storage

Alkylated Phase Change Composites for Thermal Energy Storage Based on Surface-Modified Silica Aerogels

Biomass derived carbon aerogel as an ultrastable skeleton of form-stable phase change materials for efficient thermal energy storage

Improving the phase change properties of paraffin wax by regulating the pore structure and surface properties of silica aerogel

Synthesis, Characterization and Properties of Palmitic Acid/high Density Polyethylene/graphene Nanoplatelets Composites As Form-Stable Phase Change Materials

Preparation of serpentine fiber/poly (vinyl alcohol) aerogel with high compressive strength to stabilize phase change materials for thermal energy storage

Carbon nanotubes modified graphene hybrid Aerogel-based composite phase change materials for efficient thermal storage

Assembling and characterizing of high-loading and steady-shape graphene aerogel composite phase change material with nano-AlN─as an efficient thermal conductivity enhancer

Carbonized clay pectin-based aerogel for light-to-heat conversion and energy storage

Lightweight, strong, and form-stable cellulose nanofibrils phase change aerogel with high latent heat

Aligned Channel Gelatin@nanoGraphite Aerogel Supported Form-Stable Phase Change Materials for Solar-Thermal Energy Conversion and Storage

Synthesis of a Novel Three-Dimensional Na2SO4@SiO2@Al2O3-SiO2 Phase Change Material Doped Aerogel Composite with High Thermal Resistance and Latent Heat

Enhancement of Thermal Performance of Composite Phase Change Materials by Graphite in Situ Modified Al2O3 Porous Support

Effects of carbonization temperature on the thermal characteristics of shape-stable composite phase change materials based on silica aerogel