Abstract:Diethylamine (DEA) was adopted as the low-cost template to prepare hollow fiber supported SAPO-34 molecular sieve membranes for CO2/CH4 separation. The membranes were synthesized by the secondary-growth method using ball-milled SAPO-34 seeds. Effects of seed particle size, contents of DEA and aluminum source in precursor and crystallization time on structure, morphology and separation performance of the membranes were investigated extensively. The SAPO-34 membranes induced with ball-milled seeds were more compact than those with original seeds. The increase in DEA content was beneficial to transform SAPO-11 crystals to cubic SAPO-34 crystals in the membrane layer. When the content of diethylamine is too high, the SAPO-34 membrane is not formed on the surface of the carrier. When the content of aluminum in the synthetic liquid is low, the crystallization of the molecular sieve membrane is not complete. When the content of the aluminum source is too high, the crystal grain size on the surface of the membrane is gradually reduced or even difficult to nucleate, and the thickness of the membrane layer is thinned, and it is difficult to form a continuous film. In that case, it was seen that the membrane surface became uncompacted and the membrane thickness decreased. The increased crystallization time led to thicker and denser zeolite membrane. When the precursor composition was 1.0Al2O3∶0.9P2O5∶0.6SiO2∶2.0DEA∶100H2O and the crystallization time was 36 h, the as-synthesized membrane achieved the best CO2/CH4 separation selectivity of 80 as well as CO2 permeance of 1.11×10-6 mol·m-2·s-1·Pa-1.

Synthesis of thin SAPO-34 zeolite membranes in concentrated gel

Thin SAPO-34 zeolite membranes prepared by ball-milled seeds

Efficient synthesis of thin SSZ-13 membranes by gel-less method

Preparation of high-performance zeolite NaA membranes in clear solution by adding SiO2 into Al2O3 hollow-fiber precursor

Gas Permeation Properties and Synthesis of SAPO-34 Zeolite Membranes by Secondary Growth Method

The preparation of zeolite NaA membranes on the inner surface of hollow fiber supports

Thin Carbon/sapo-34 Microporous Composite Membranes for Gas Separation

Diethylamine template-directed synthesis of hollow fiber supported SAPO-34 membranes

Highly H 2 permeable SAPO-34 membranes by steam-assisted conversion seeding

Fast synthesis of thin SSZ-13 membranes by a hot-dipping method

Preparation of zeolite MFI membranes on alumina hollow fibers with high flux for pervaporation

Synthesis of SAPO-34 Molecular Sieve Membranes by Steam-assisted Conversion Seeding and Their Characterization

Seed-Free Synthesis of Highly Permeable Zeolite Naa Membranes Through Deposition of Aptes-Functionalized Alumina Particles on Macroporous Supports

Synthesis and Low-Temperature Detemplation of High-Silica Mfi Zeolite Membranes

Effects of the synthesis hydrogel on the formation of zeolite LTA membranes

Synthesis of A Sapo-34 Membrane on Macroporous Supports for High Permeance Separation of A Co2/Ch4 Mixture

Manipulation of the Surface Microstructure and Its Effects on the Flux of NaA Zeolite Membranes in Pervaporation

Improved Synthesis of Hollow Fiber SSZ‐13 Zeolite Membranes for High‐Pressure CO2/CH4 Separation

A Facile Preparation of High Flux NaA Zeolite Membranes by Direct Secondary Growth of Wet Gel Layer

Preparation of Zeolite NaA Membranes on Macroporous Alumina Supports by Secondary Growth of Gel Layers

Synthesis of SAPO-34 Zeolite Membrane: Influence of Sources of Silica