Exploring Phase Transformation Mechanisms in Maraging‐300 Steel During Ageing Beyond Widely Applied Temperature Parameters
Jean Jefferson Moraes da Silva,Igor Frota de Vasconcelos,Carlos Augusto Silva de Oliveira,Pedro Henrique Lamarão Souza,Rodrigo de Carvalho Paes Loureiro,Marcos Natan da Silva Lima,Samuel Filgueiras Rodrigues,Hamilton Ferreira Gomes de Abreu
DOI: https://doi.org/10.1002/srin.202300871
IF: 2.1258
2024-06-07
steel research international
Abstract:Maraging steels reach peak strength when aged at ≈480 °C. Research has explored treatments at other temperatures to enhance toughness and magnetic properties. Using various techniques, this study investigates phase transformation in Maraging‐300 steel aged at 520, 560, and 600 °C. Precipitation of intermetallic compounds, crucial for mechanical improvements, occurred similarly to 480 °C aging within the first hour. Coexistence of precipitates and austenitic phase is observed, suggesting a crystalline/magnetic transition zone at longer times and higher temperatures. Maraging steels achieve the highest strength limit when aged around 480 °C. Some research has been carried out on this treatment at temperatures different from 480 °C to improve the toughness and magnetic properties of this metal. This research uses Mössbauer spectroscopy, X‐ray diffraction (XRD), hardness measurements, and transmission electron microscopy (TEM) to investigate the phase transformation process of solution‐treated Maraging‐300 steel specimens aged at 520, 560, and 600 °C. The results indicate that the precipitation of intermetallic compounds, which are responsible for the improvement of mechanical properties, occurs similarly to precipitation at the temperature of 480 °C within the first hour of ageing. The coexistence of precipitates and the austenitic phase is detected, and a crystalline/magnetic transition zone is suggested in the material for longer times and higher ageing temperatures.
metallurgy & metallurgical engineering